OBJECTIVE To study the biocompatibility of skin reproductive membrane. METHODS According to ISO’s standards, the extractions of the skin reproductive membrane were prepared, and the acute systematic toxicity test, primary skin irritant test, cytotoxicity test, gene expression of type I collagen and fibronectin were detected to evaluate the biocompatibility of skin reproductive membrane. RESULTS All of those tests showed negative results. CONCLUSION The skin reproductive membrane has excellent biocompatibility in the level of the systematic, cellular and molecular biology.
Objective To investigate the influence of different dose levels of hydroxyapatite/tricalcium phosphate (HA/TCP) on the proliferation and alkalinephosphatase (ALP) activity of rabbit osteoblasts. Methods Three different doselevels of HA/TCP (10%, 40%, 70%) were co-cultivated with rabbit osteoblasts respectively. The proliferation and ALP expression capacity of osteoblasts were examined with MTT method and enzyme histochemistry once every 24 hours until 5 days. Three control groups of other materials were treated and examined in the sameway: rabbit osteoblasts as normal control; polyvinylchloride as positive control; titanium alloy as negative control. Results There was remarkable timeeffect relationship in the proliferation of osteoblasts. Ten percent HA/TCP did not affect osteoblasts growth while 40% HA/TCP could slow the cell growth rate down though time-effect relationship still existed. The proliferation of osteoblasts stagnated when co-cultivated with 70% HA/TCP. On the other hand, 10% HA/TCP could cause reversible damage on ALP activity of osteoblasts, whereas when the dose was40%, and the cultivation lasted 6 days the damage was irreversible. Three different dose levels of titanium alloy (10%, 40%, 70%) had no effect on the proliferation or ALP activity of osteoblasts. Conclusion Dosage is an important factor affecting the biocompatibility evaluation of biomaterial. It suggests that dose choosing should be more specified upon each individual biomaterial. It also indicates that ALP may be a good supplementary index of the cell compatibility of material.
To explore the histological and the hematological change of rabbits after implanting novel injectable artificial nucleus prostheses, and to evaluate the biological safety. Methods In accordance with Biological Evaluation of Medical Devices, materials of polyurethane, sil icone rubber and macromolecular polyethylene for medical use were made into short column 1 cm in length and 0.3 cm in diameter. Forty-eight SPF New Zealand white rabbits weighing 2.5-3.0 kg were used, and cavity 1 cm in depth was made in the area 2 cm away from the spinal midl ine by separating muscle.Then according to different material being implanted, the rabbits were divided into 3 groups (n=16): Group A, polyurethane; group B, sil icone rubber; group C, macromolecular polyethylene for medical use as negative control. General condition of the rabbits was observed after operation. Gross and histology observation were conducted 1, 4, 12 and 26 weeks after operation. Blood routine, biochemical function and electrolyte assays were performed 26 weeks after operation to observe pathological changes of organs. Meanwhile, physicochemical properties of the materials were detected, and the material in the same batch was used as negative control. Results All rabbits survived until the end of experiment, and all wounds healed by first intention. In each group, red swollen muscles were observed 1 week after operation and disappeared 4 weeks after operation, connective tissue around the implanted materials occurred 12 and 26 weeks after operation. At 26 weeks after operation, there were no significant differences among three groups in blood routine, biochemical function and electrolyte assays (P gt; 0.05). Organs had smooth surface without ulceration, ecchymosis, obvious swell ing, hyperemia or bleeding, and nodules. There were no significant differences among three groups in percentage weight of each organ (P gt; 0.05). Histology observation: granulation tissue prol iferation and inflammatory cell infiltration were observed in each group 1 week after operation, fibrous capsule formation around the materials and the disappearance of inflammatory cell infiltration were evident 4 weeks after operation, cyst wall grewover time and achieved stabil ity 12 weeks after operation. The inflammatory response and the fiber cyst cavity of groups A and B met the standard of GB/T 16175 and were in l ine with group C. No specific pathological changes were discovered in the organs 26 weeks after operation. For group A, no significant difference was evident between before and after material implantation in terms of weight average molecular weight, number average molecular weight, tensile strength at break and elongation at break (P gt; 0.05). For group B, no significant difference was evident between before and after material implantation in shore hardness (P gt; 0.05). Conclusion Novel injectable nucleus pulposus prostheses do not damage local tissue and function of organs, but provide good biocompatibil ity and biological safety.
Objective To choose the best procedure on preparation of acellularbovine pericardium (ABP) guided bone regeneration (GBR) material. Methods The BP was decellularized with 0.25% Trypsin+0.5% Triton X-100. The acellular bovine pericardiums (ABPs) were treated with phosphatebuffered saline(PBS) (group A), 95% glycerol (group B), EDAC (group C), and EDAC and 95% glycerol (group D) respectively. The treated ABPs were implanted subcutaneously in the back of SD rats respectively at random and no material was implanted as control. Seven rats were sacrificed at 2 weeks, twelve at 4 weeks, twelve at 8 weeks, seven at 16 weeks. Local reaction was studied grossly. The amount of antigen presenting cell (APC) and the percentage of ABP degeneration were reckoned by images analysis system. Results The ABPs were replaced by fibroblasts completely in group A at 8 weeks， in group C at 16 weeks, but only less than 50% till 16 weeks in groups B and D. In all groups, the depth of surrounding fibres attenuated timedependingly. The APC amount of the groups B and D was higher than that of the control group, and the ABP of the groups B and D degraded partly at 16 weeks. Conclusion The ABP treated with EDAC can be replaced by the surrounding tissues and has good biocompatibility.
Objective To investigate the biocompatibility of p(3HB-co-3HH) and marrow mesenchymal stell cells (MSCs).Methods MSCs were inoculated to p(3HB-co-3HH), and then cultured for 2-4 weeks in vitro and embedded for 2 weeks in vivo. The growth, proliferation, morphology and phenotype properties of MSCs were observed by use of phase contrast microscope, electron microscope, HE staining and staining of type Ⅰ collagen. Results p(3HB-co-3HH) hadgood compatibility. The inoculated MSCs could be well-distributed, attached well and obtain the phenotype of MSCs in p(3HB-co-3HH). After osteogenic inducer were added, MSCs differentiated to osteoblasts and secreted matrix. Type Ⅰ collagen was stained positively by immunohistochemical techenique. Conclusion The above results demonstrate that there is satisfactory biocompatibility betweenp(3HB-co-3HH) and MSCs.
Objective To investigate the biocompatibility of acellular urinary bladder submucosa (AUBS). Methods The acellular collagen matrix of human urinary bladder submucosa was developed using freeze-thawed enzymatic treatment and freeze-drying technique. Human oral keratinocytes were cultured and seeded on AUBS at a density of 2×106/ml in vitro.The proliferation of the cells were observed. Pockets were created in the abdominal muscle wall of 18 SD rats. AUBS in size 1 cm×1 cm was implanted into the pocket. The grafts were observed by light microscope 3, 6, 10, 14, 21 and 28 days after operation. Results AUBSmainly consisted of collagen fibers with a three-dimensional network structure. After the oral keratinocytes were seeded, continous oral epithelium layer was formed on the surface of AUBS after 10 days in vitro. Histological observation of the grafted AUBS showed progressive cell infiltration at 6 days. New capillaries formed at 14 days. The collagen fibers arranged regularly at 28 days after implantation. Conclusion Freeze-dried AUBS may be used as a suitable scaffold for tissue regeneration, which can induce cell proliferation both in vivo and in vitro and has good biocompatibilty.
Objective To evaluate the biocompatibility and in vivo degradation of novel chest wall prosthesis materials and provide some data for their clinical application. MethodsAccording to the standard for the biological evaluation of the medical devices, several tests were performed to evaluate the tissue toxic effects induced by polydioxanone (Group A), chitosan (Group B), and hydroxyapitite/collagen (Group C),which were tested as component materials of the chest wall prosthesis. In the hemolysis test, 0.2 ml of the anticoagulant rabbit blood was added to the component materials and the normal saline (negative control) and to the distilled water(positive control). Five samples were made in each group. Absorbency was measured and the hemolysis rate was determined. In the acute systemic toxicity test, 20 mice were randomly divided into 4 groups (Groups A, B and C, and the normal saline group, n=5). The leaching liquid (50 ml/kg) was injected through the caudal vein, which was observed at 24, 48 and 72 hours. In the pyrogen test, 12 rabbits were randomly divided into 4 groups (Groups A, B, C and the normal saline group, n=3) the leaching liquid(10 ml/kg) was injected through the ear vein,and the body temperature was recorded within 3 hours. In the in vivo degradable test, the component materials (10 mm×10 mm) were implanted in 12 rabbits at 2, 4, 8, 12, 16 and 24 weeks, respectively, after operation. Two rabbitswere sacrificed for the macroscopic and the microscopic examinations. Results The chest wall component materials had no hemolytic reaction, no acute systemic toxicity, and no pyrogen reaction. The results demonstrated that the implanted materials had only a mild inflammatory reaction during the early days of the grafting, which subsided gradually. There was no tissue denaturation, necrosis or pathological hyperplasia when the prosthesis materials were degraded. Conclusion The degradable materials of the chest wall prosthesis have a good biocompatibility and agreat biological safety though their surgical application still requires a further clinical research.
Objective To investigate the biocompatibility of diamond-like carbon(DLC) coated NickelTitanium shape memory alloy with osteoblasts cultured invitro. Methods Rabbit’s osteoblasts were incubated with DLCcoated NickelTitanium shape memory alloy disks and uncoated ones of equal size for 5 days. The control group（without shape memory alloy in culture media） was performed simultaneously. The cultured cells were counted and graphed. The samples from culture media were collected and the concentrations of alkaline phosphatase (ALP) and nickel（Ni2+） were measured from the 1st to 5th day respectively. Results The proliferation of osteoblasts and the concentration of ALP in both DLC-coated group and control gruop was higher than uncoated group. The proliferation of osteoblasts on the 3rd, 4th, and 5th day in both DLC-coatedgroup and control group was significantly higher than that in the uncoated group(P＜0.05). The concentration of ALP in DLC-coated group on the 2nd, 3rd, and 5th day and in the control group on the 3rd, 4th, and 5th day was significantly higher than that in the uncoated group(P＜0.05). The concentration of Ni2+ on the 3rd, 4th, and 5th day was significantly lower than that in the uncoated group(P＜0.05). Conclusion DLC- coated NickelTitanium shape memory alloys appears to have better biocompatibility with osteoblast cultured in vitro compared to uncoated ones.
ObjectiveTo study the biocompatibility of bioprosthetic heart valve material with a non-glutaraldehyde-based treatment, and to provide the safety data for the clinical application. MethodsAll the tests were conducted according to GB/T16886 standards. The in vitro cytotoxicity was determined by methyl thiazolyl tetrazolium assay. Fifteen guinea pigs were divided into a test group (n=10) and a control group (n=5) in the skin sensitization test. Three New Zealand white rabbits were used in the intradermal reactivity test. Five sites on both sides of the rabbit back were set as test sites and control sites, respectively. In the acute systemic toxicity test, a total of 20 ICR mice were randomly assigned to 4 groups: a test group (polar medium), a control group (polar medium), a test group (non-polar medium) and a control group (non-polar medium), 5 in each group. Forty SD rats were divided into a test group (n=20) and a control group (n=20) in the subchronic systemic toxicity test. ResultsThe viability of the 100% extracts of the bioprosthetic heart valve material with a non-glutaraldehyde-based treatment was 75.2%. The rate of positive reaction was 0.0%. The total intradermal reactivity test score was 0. There was no statistical difference in the body weight between the test group and control group in the acute systemic toxicity test. There was no statistical difference in the body weight, organ weight, organ weight/body weight ratio, blood routine test or blood biochemistry between the test group and control group in the subchronic systemic toxicity test. ConclusionThe bioprosthetic heart valve material with a non-glutaraldehyde-based treatment has satisfying biocompatibility, which conforms to relevant national standards. The material might be a promising material for application in valve replacement.
Objective To summarize the research progress of biocompatibility and surface modification of nickel titanium shape memory alloys (Ni-Ti SMA). Methods The relative researches about Ni-Ti SMA at home and abroad were reviewed, collated, analyzed, and summarized. Results At present, Ni-Ti SMA as an internal fixation material has been widely used in clinic. It has the following advantages: the super elasticity, the shape memory characteristic, the good wear resistance, and the strong corrosion resistance. It also can effectively avoid the internal fixator rupture caused by stress shielding. After surface modification, the biocompatibility of Ni-Ti SMA has been improved. Conclusion The Ni-Ti SMA is the most promising alloy material for the long-term internal fixator because of its excellent material properties.