Objective To investigate the effect of homograft of marrow mesenchymal stem cells (MSCs) seeded onto poly-L-lactic acid (PLLA)/gelatin on repair of articular cartilage defects. Methods The MSCs derived from36 Qingzilan rabbits, aging 4 to 6 months and weighed 2.5-3.5 kg were cultured in vitroand seeded onto PLLA/gelatin. The MSCs/ PLLA/gelatin composite was cultured and transplanted into full thickness defects on intercondylar fossa. Thirty-six healthy Qingzilan rabbits were made models of cartilage defects in the intercondylar fossa. These rabbits were divided into 3 groups according to the repair materials with 12 in each group: group A, MSCs and PLLA/gelatin complex(MSCs/ PLLA/gelatin); group B, only PLLA/gelatin; and group C, nothing. At 4,8 and 12 weeks after operation, the gross, histological and immunohistochemical observations were made, and grading scales were evaluated. Results At 12 weeks after transplantation, defect was repaired and the structures of the cartilage surface and normal cartilage was in integrity. The defects in group A were repaired by the hylinelike tissue and defects in groups B and C were repaired by the fibrous tissues. Immunohistochemical staining showed that cells in the zones of repaired tissues were larger in size, arranged columnedly, riched in collagen Ⅱ matrix and integrated satisfactorily with native adjacent cartilages and subchondral bones in group A at 12 weeks postoperatively. In gross score, group A(2.75±0.89) was significantly better than group B (4.88±1.25) and group C (7.38±1.18) 12 weeks afteroperation, showing significant differences (P＜0.05); in histological score, group A (3.88±1.36) was better than group B (8.38±1.06) and group C (13.13±1.96), and group B was better than group C, showing significant differences (P＜0.05). Conclusion Transplantation of mesenchymal stem cells seeded onto PLLA/gelatin is a promising way for the treatment of cartilage defects.
Objective To explore the relationship of the limited resource of the autologous bone marrow mesenchymal stem cells (MSCs) in articularcavity to the treatment results of full-thickness articular cartilage defect, and to investigate whether the extrogenous sodium hyaluronate(SH) promotes the migration of MSCs cultured in vitro tothe articular defect in vivo. Methods Sixty-six Japan rabbits were made the model of the full-thickness articular cartilage defect (5 mm width and 4 mm depth).The autologous MSCs were extracted from the rabbit femur, cultured in vitro, labeledby Brdu, and injected into the injured articular cavity with or without SH. Theexperiment was divided into 4 groups; group A (MSCs and SH, n=15); group B (MSCs, n=15); group C (SH, n=18); and group D (non-treatment, n=18). The morphologic observation was made by HE staining, Mallory staining and immunohistochemical staining after 5 weeks, 8 weeks and 12 weeks of operation. Results There were significant differences in the thickness of repairing tissue between group A and group B(Plt;0.01); but there were no significant differences between group A and group C, and between group B and group D(P＞0.05). Thehistological observation showed that the main repairing tissue was fibrocartilage in group A and fiber tissue in group B. Conclusion MSCs cultured in vitro and injected into the articular cavity can not improve the treatment results of the articular cartilage defect. Extrogenous SH has effect on repairing cartilage defect. The extrogenous SH has no effect on the chemotaxis of the MSCs, and on the collection of MSCs into the joint defect.
Objective To explore the methods of repairing cartilagedefects and to introduce the clinical experience with the autologous osteochondral transplantation. Methods Twenty-five patients with chondral and osteochondral defects of the weight-bearing surfaces were treated by the autologous osteochondral transplantation for the repair of the chondral and osteochondral defects of the unweightbearing surfaces under arthroscope. According to the shape of the defects, the different dimensions of the osteochondral autograft were selected. All the patients began the training of the continuous passive motion after operation. Six weeks after operation, the patients began to walk in the weightbearing habitus. However, in the control group, another 25 patients were retrospectively analyzed, who had chondral and osteochondral defects of the weight-bearing surfaces but were treated only by the cleaning and drilling procedures. The scores evaluated bythe Brittberg-Peterson scoring scale of the 2 group were 98.65±9.87 and 96.98±8.94 respectively. Results The follow-upfor 3-24 months after operation revealed that the treated knee joint had a goodmotion extent. The pain was obviously alleviated. Based on the longitudinal study with the three-dimensional spoiled magnetic resonance imaging (MRI), the signal intensity of the repaired tissues approached to the normal condition. The scores evaluated by the Brittberg-Peterson scoring scale were almost zero 3 monthsafter operation in the experimental group, and the scores were 58.48±6.98 inthe control group. There were significant differences between the experimental group and the control group(P＜0.01). Conclusion Autologous osteochondral transplanation under arthroscope is a good curative method for the cartilage defects, with advantages of minimal invasiveness and avoidanceofrejections resulting from allografts. However, its long-term effect needs to befurther studied. The conventional therapies including cleaning and drilling are useful in alleviating the symptoms.
Objective To investigate the clinical application of periosteal autograft in repair of cartilage defect caused by osteoarthritis of knee. Methods From 1996 to 1999, 36 knees of cartilage defect of knee joint in 28 cases were treated. In the operation, the cracked degenerative cartilage was removed before free periosteum from tibia was transplanted to repair the defect, and the meniscuses in 8 knees of the 36 knees were reconstructed. After operation, early continuous passive movement was adopted for 4 weeks, and 8 knees with reconstruction ofthe meniscus were immobilized by plaster splint for 7 days after operation and before passive movement. All of the cases were followed up for 1 to 4 years before clinical evaluation in symptoms, signs and radiological findings. Results The general satisfactory rate was 86.1%, in which the function was excellent in 22 knees and good in 9 knees. Conclusion The periosteal autograft is a good choice for repairing cartilage defect due to osteoarthritis, with a satisfactory outcomein the short term.
Objective To explore the effect of tissue engineered cartilage reconstructed by using sodium alginate hydrogel and SIS complex as scaffold material and chondrocyte as seed cell on the repair of full-thickness articular cartilage defects. Methods SIS was prepared by custom-made machine and detergent-enzyme treatment. Full-thickness articularcartilage of loading surface of the humeral head and the femoral condyle obtained from 8 New Zealand white rabbits (2-3weeks old) was used to culture chondrocytes in vitro. Rabbit chondrocytes at passage 4 cultured by conventional multipl ication method were diluted by sodium alginate to (5-7) × 107 cells/mL, and then were coated on SIS to prepare chondrocyte-sodium alginate hydrogel-SIS complex. Forty 6-month-old clean grade New Zealand white rabbits weighing 3.0-3.5 kg were randomized into two groups according to different operative methods (n=20 rabbits per group), and full-thickness cartilage defect model of the unilateral knee joint (right or left) was establ ished in every rabbit. In experimental group, the complex was implanted into the defect layer by layer to construct tissue engineered cartilage, and SIS membrane was coated on the surface to fill the defect completely. While in control group, the cartilage defect was filled by sodium alginate hydrogel and was sutured after being coated with SIS membrane without seeding of chondrocyte. General condition of the rabbits after operation was observed. The rabbits in two groups were killed 1, 3, 5, 7, and 9 months after operation, and underwent gross and histology observation. Results Eight rabbits were excluded due to anesthesia death, wound infection and diarrhea death. Sixteen rabbits per group were included in the experiment, and 3, 3, 3, 3, and 4 rabbits from each group were randomly selected and killed 1, 3, 5, 7, and 9 months after operation, respectively. Gross observation and histology Masson trichrome staining: in the experimental group, SIS on the surface of the implant was fused with the host tissue, and the inferface between them disappeared 1 month after operation; part of the implant was chondrified and the interface between the implant and the host tissue was fused 3 months after operation; the implant turned into fibrocartilage 5 months after operation; fiber arrangement of the cartilage in theimplant was close to that of the host tissue 7 months after operation; cartilage fiber in the implant arranged disorderly andactive cell metabol ism and prol iferation were evident 9 months after operation. While in the control group, no repair of thedefect was observed 9 months after operation. No obvious repair was evident in the defects of the control group within 9months after operation. Histomorphometric evaluation demonstrated that the staining intensity per unit area of the reparative tissue in the defect of the experimental group was significant higher than that of the control group at each time point (P lt; 0.05), the chondrification in the experimental group was increased gradually within 3, 5, and 7 months after operation (P lt; 0.05), and it was decreased 9 months after operation comparing with the value at 7 months after operation (P lt; 0.05). Conclusion Constructed by chondrocyte-sodium alginate hydrogel-SIS in complex with surficial suturing of SIS membrane, the tissue engineered cartilage can in-situ repair cartilage defect, promote the regeneration of cartilage tissue, and is in l ine with physiological repair process of articular cartilage.
It is very difficult to repair large articular cartilage defect of the hip. From May 1990 to April 1994, 47 hips in 42 patients of large articuler cartilage defects were repaired by allograft of skull periosteum. Among them, 14 cases, whose femoral heads were grade. IV necrosis, were given deep iliac circumflex artery pedicled iliac bone graft simultaneously. The skull periosteum had been treated by low tempreturel (-40 degrees C) before and kept in Nitrogen (-196 degrees C) till use. During the operation, the skull periosteum was sutured tightly to the femoral head and sticked to the accetabulum by medical ZT glue. Thirty eight hips in 34 patients were followed up for 2-6 years with an average of 3.4 years. According to the hip postoperative criteria of Wu Zhi-kang, 25 cases were excellent, 5 cases very good, 3 cases good and 1 case fair. The mean score increased from 6.4 before operation to 15.8 after operation. The results showed, in compare with autograft of periosteum for biological resurface of large articular defect, this method is free of donor-site morbidity. Skull periosteum allograft was effective for the treatment of large articular cartilage defects in hip.
Objective To investigate the performance of loading naringin composite scaffolds and its effects on repair of osteochondral defects. Methods The loading naringin and unloading naringin sustained release microspheres were prepared by W/O/W method; with the materials of the attpulgite and the collagen type I, the loading naringin, unloading naringin, and loading transforming growth factor β1 (TGF-β1) osteochondral composite scaffolds were constructed respectively by " 3 layers sandwich method”. The effect of sustained-release of loading naringin microspheres, the morphology of the composite scaffolds, and the biocompatibility were evaluated respectively by releasingin vitro, scanning electron microscope, and cell counting kit 8. Forty Japanese white rabbits were randomly divided into groups A, B, C, and D, 10 rabbits each group. After a osteochondral defect of 4.5 mm in diameter and 4 mm in depth was made in the intercondylar fossa of two femurs. Defect was not repaired in group A (blank control), and defect was repaired with unloading naringin composite scaffolds (negative control group), loading naringin composite scaffolds (experimental group), and loading TGF-β1 composite scaffolds (positive control group) in groups B, C, and D respectively. At 3 and 6 months after repair, the intercondylar fossa was harvested for the general, HE staining, and toluidine blue staining to observe the repair effect. Western blot was used to detect the expression of collagen type II in the new cartilage. Results Loading naringin microspheres had good effect of sustained-release; the osteochondral composite scaffolds had good porosity; the cell proliferation rate on loading naringin composite scaffold was increased significantly when compared with unloading naringin scaffold (P<0.05). General observation revealed that defect range of groups C and D was reduced significantly when compared with groups A and B at 3 months after repair; at 6 months after repair, defects of group C were covered by new cartilage, and new cartilage well integrated with the adjacent cartilage in group D. The results of histological staining revealed that defects were filled with a small amount of fibrous tissue in groups A and B, and a small amount of new cartilage in groups C and D at 3 months after repair; new cartilage of groups C and D was similar to normal cartilage, but defects were filled with a large amount of fibrous tissue in groups A and B at 6 months after repair. The expression of collagen type II in groups C and D was significantly higher than that in groups A and B (P<0.05), but no significant difference was found between groups C and D (P>0.05). Conclusion Loading naringin composite scaffolds have good biocompatibility and effect in repair of rabbit articular osteochondral defects.
ccording to the characteristics of periosteum which have a copacity for regrowth of cartilage,free autogenous osteoperiosteal grafts taken from the medial side of the metaphsis of the tibia had beenused to reconstruct the osteochondral defects of the articular surface of the knee joint. The mothod wasillustrated by five cases which included of osteochondritis dissecans, subchondral osteonecrosis and oldfracture of the patella. By the period of 16-26 monthes follow up, using knee function...
Objective To explore the preparing methods in vitro and test the cl inical appl icabil ity of implantation in vivo of bone marrow stromal stem cells (BMSCs)-biphasic scaffold to repair defects of cartilage and subchondral bone and tocompare the differences in repaired outcomes of composite, single biphasic scaffold and rabbits themselves. Methods The upper chondral phase and the lower osseous phase of the plugs, using poly-lactic-co-glycol ic acid (PLGA), hydroxyapatite (HA), and other biomaterials, were fused into carrier scaffold, on which collagen type I (Col I) was coated. The surface and inner structure of bi phasic scaffold were observed under scanning electron microscope (SEM). BMSCs was isolated from the bone marrow of tibia and femurs of young New Zealand rabbits using centrifuging and washing, and their morphologies and adherences were observed everyday. Then BMSCs were inoculated on the surface of scaffold to form BMSCs-scaffold composites. Osteochondral defects were surgically created on articular surface of femoral intercondyles of 30 New Zealand rabbits, which were divided into groups A, B and C. In group A, a bi phasic osteochondral composite were implanted into defect, BMSCs and biphasic cyl indrical porous plug of PLGA-HA-Col I in group B, and group C was used as a control without implant. Specimens were harvested to make macroscopic and histological observations at the 1st, 3rd, 6th, and 9th months after operation respectively; meanwhile immunohistological and micro-computed tomography (micro CT) examinations were performed and graded at the 9th month after operation. Results SEM showed an excellent connection of holes in the biphasic scaffold infiltrated by Col I. Optical microscopy and SEM showed a good growth of BMSCs in scaffold without obvious cellular morphological changes and an accumulation in the holes. Macroscopic samples showed a resistant existence of defects of group C within 9 months; the scaffold completely degenerated and chondral-l ike tissue formed on articular surface with partly collapses and irregular defects in group A; and smoother surface without collapses and approach to normal with texture of new regeneration in group B. There were statistically significant differences in macroscopic results (P lt; 0.001), group B was superior to group A, and group C was the worst. The micro CT showed good repairs and reconstruction of subchondral bone, with a acceptable integration with newborn chondral-l ike tissue and host bone in group B. Quantificational analysis of relevantparameters showed no significant differences. Histological results showed inflammations located in defects at the 1st month, new tissue grew into scaffold at the 3rd month; new chondral-l ike tissue crept on the margin of defects and biphasic scaffold degenerated completely at the 6th month, and lots of collagen formed in subchondral bone with major fibrocartilage on chondralarea at the 9th month after surgery in groups A and B. In groups A and B, immunohistological observations were weak positive for Col II and positive for Col I. Conclusion Biphasic scaffold implanted in body can induce and accelerate repair of defects of articular cartilages which are mainly filled with fibrocartilage, especially for subchondral bone. Scaffold combined with BMSCs has the best repairing effects 9 months after implantation.