Objective To investigate the feasibility of a new kind of porous β tricalcium phosphate (β-TCP) as a scaffold for the bone tissue engineering Methods The inverted phase contrast microscope was used to observe the growth of the marrow mesenchymal stem cells (MSCs) in the experimentalgroup and the control group at 10 days.In the experimental group, the MSCs were cultured with β-TCP(3 mm×3 mm×3 mm) in the 24-hole cultivation board, and in the control to control group, only MSCs were cultivated. The scanning electron microscope was used to observe growth of MSCs at 6 days. Cultivated with β-TCP at 3, 6, 9, 12 days, the MTT assay was used to judge the biocompatibility. The cytotoxicity was analyzed with the method that used the different density(100%， 50%， 10%， 1%，0%) leaching liquor gained from β-TCP to raise MSCs. MSCs were induced into the osteoblasts and were mixed with β-TCP, and the composite was used to repair a large radius bone defect in the rabbit. The specimens were made at 2,6,12 weeks. The histology imageology, and the radionuclide bone scan were used to analyze the bone formation. Results Some MSCs had a good adherence 4 hours after MSCs were inoculated and had a complete adherence at 12 hours. The cells were shaped like polyangle, spindle or converge monolayer after 8-10 days. The cells in the two groups had no difference. The cell adhesion was good, when observed by the inverted phase contrast microscope and the scanning electron microscope at 6 days. MTT showed that the absorbance (A)was not statistically different between the experimental group and the control group (P＞0.05); the different density leaching liquor had no cytotoxicity at the different time points. Histology, X-ray, and CT tomograph showed that itcould repair the large radius bone defect in the rabbit and its in vivo degradationrate was the same as the bone formation rate. Conclusion The new porous β-TCP has a unique three dimensional (3D) stereochemical structure and superordinary physicochemical property, and so it is a good scaffold for the bone tissue engineering.
Bioactive glass (BG) has been widely used in the preparation of artificial bone scaffolds due to its excellent biological properties and non-cytotoxicity, which can promote bone and soft tissue regeneration. However, due to the brittleness, poor mechanical strength, easy agglomeration and uncontrollable structure of glass material, its application in various fields is limited. In this regard, most current researches mainly focus on mixing BG with organic or inorganic materials by freeze-drying method, sol-gel method, etc., to improve its mechanical properties and brittleness, so as to increase its clinical application and expand its application field. This review introduces the combination of BG with natural organic materials, metallic materials and non-metallic materials, and demonstrates the latest technology and future prospects of BG composite materials through the development of scaffolds, injectable fillers, membranes, hydrogels and coatings. The previous studies show that the addition of BG improves the mechanical properties, biological activity and regeneration potential of the composites, and broadens the application of BG in the field of bone tissue engineering. By reviewing the recent BG researches on bone regeneration, the research potential of new materials is demonstrated, in order to provide a reference for future related research.
Objective To review the research progress of osteoblastextracellular matrix(ECM) and its application in bone tissue engineering. Methods The recentrelated literatures were extensively reviewed. Results The ECM was complex in its components. The configuration of cell and cell’s adhesion, migration, proliferation, and differentiation were subject to the ECM. The bioactivity of the tissue engineering products was revealed by ECM, which predicted the product’s efficiency in clinic application. Conclusion ECM has the potential to become the effective index in evaluating tissue engineered products.
ObjectiveTo review the application and research progress of in vivo bioreactor as vascularization strategies in bone tissue engineering. MethodsThe original articles about in vivo bioreactor that can enhance vascularization of tissue engineered bone were extensively reviewed and analyzed. ResultsThe in vivo bioreactor can be created by periosteum, muscle, muscularis membrane, and fascia flap as well as biomaterials. Using in vivo bioreactor can effectively promote the establishment of a microcirculation in the tissue engineered bones, especially for large bone defects. However, main correlative researches, currently, are focused on animal experiments, more clinical trials will be carried out in the future. ConclusionWith the rapid development of related technologies of bone tissue engineering, the use of in vivo bioreactor will to a large extent solve the bottleneck limitations and has the potential values for clinical application.
Objective To fabricate a nanohydroxyapatite-chitosan(nano-HA-CS) scaffold with high porosity by a simple and effective technique and to evaluate the physical and chemical properties and the cytocompatibility of the composite scaffold. Methods The threedimensional nano-HA-CS scaffolds with high porosity were prepared by the in situ hybridization-freeze-drying method. The microscopic morphology and components of the composite scaffolds were analyzed by the scanning electron microscopy (SEM), the transmission electron microscopy（TEM）, the X-ray diffraction（XRD）examination, and the Fourier transformed infrared spectroscopy（FTIR）. The calvarial osteoblasts were isolated from the neonatal Wistar rats. The serial subcultured cells (3rd passage) were respectively seeded onto the nanoHACS scaffold and the CS scaffold, and then were cocultured for 2, 4, 6 and 8 hours. At each time point,four specimens from each matrix were taken to determine the celladhesion rate. The cell morphology was observed by the histological staining and SEM. Results The macroporous nanoHACS scaffolds had a feature of high porosity with a pore diameter from 100 to 500 μm (mostly 400500 μm). The scaffolds had a high interval porosity; however, the interval porosity was obviously decreased and the scaffold density was increased with an increase in the contents of CS and HA. The SEM and TEM results showed that the nanosized HA was synthesized and was distributed on the pore walls homogeneously and continuously. The XRD and FTIR results showed that the HA crystals were carbonatesubstituded and not wellcrystallized. The cytocompatibility test showed that the seeded osteoblasts could adhere the scaffolds, proliferating and producing the extracellular matrix on the scaffolds. The adherence rate for the nanoHACS scaffolds was obviously higher than that for the pure CS scaffolds. Conclusion The nano-HA-CS scaffolds fabricated by the in situ hybridization-freeze-drying method have a good physical and chemical properties and a good cytocompatibility; therefore, this kind of scaffolds may be successfully used in the bone tissue engineering.
Objective To investigate effects of the basic fibroblast growth factor (bFGF) and fibronection (FN) on the osteoblast adhesion on the bio-derived bone. Methods The third generation of the osteoblast was treated with bFGF 0.1, 1, 10, and 100 ng/ml, respectively, and then was seeded in the bioderived bone, which had been modified with FN 0.1, 1, 10, and 100 μg/ml, or Polylysine, respectively. The cell adhesion was measured by the MTT assay. The cell density and the cell appearance were observed by the scanning electron microscope. The abovementioned procedures were repeated by an application of the GRGDS peptide. Results Both FN and bFGF could enhance the osteoblast adhesion efficiency on the bioderived bone (Plt;0.05). However, the osteoblast adhesion efficiency could be significantly strengthened bya combined use of FN and bFGF. FN and bFGF had a significant synergistic effectin statistics (Plt;0.01), but Polylysine and bFGF had no such synergistic effect (P＞0.05). The combined use of FN and bFGF had a better effect on the cell density and the cell appearance than either of them when observed with the scanning electron microscope. Adhesion efficiency generated by the combined use of FN and bFGF was significantly blocked by the application of the GRGDS peptide. Conclusion The combined use of FN and bFGF has a significant synergistic effect on the osteoblast adhesion efficiency on the bioderived bone. This effect is probably mediated by the RGD-integrin α5β1 pathway.
Objective To evaluate the feasibility of poly-L-lactide(PLLA)/porcinederived xenogeneic bone(PDXB) composite as a scaffold for the bone tissue engineering. Methods The film and the scaffold of the PLLA-PDXB composite were respectively prepared by a solution casting method and a solution casting-particle leaching method. The composite film and scaffold were further treated by the surface alkaline hydrolysis. The surface morphology of the composite was observed by the scanning electron microscopy, and hydrophilicity degree of the composite was measured. The OCT-1 osteoblastlike cells were cultured and amplified in vitro as the seeding cells, which werethen implanted on the film and scaffold. The adherence rate, adherence shape,proliferating activity, and growing morphology of the OCT-1 osteoblastlikecells were observed on the film. Results The PDXB particle 50 μm in diameter on average had a similar phase structure to that of hydroxyapatite. But its Ca/P ratio was lower than that of hydroxyapatite. After the surface alkaline hydrolysis, the PDXB particle could be exposed on the surface of the PLLA-PDXB composite. The surface roughness and hydrophilicity of the PLLAPDXB composite were obviously enhanced. The cell adherence rate and the cell proliferation activity of the PLLAPDXB composite were higher than those of the pure PLLA material. The cells tended to grow on the exposed surface of the PDXB particles. The cells seeded on the composite scaffold could migrate to the inside of the composite scaffold and grew well. Conclusion The PLLA-PDXB composite has a good cell affinity, and this kind of composite can hopefullybecome a new scaffold material to be used in the bone tissue engineering.
Objective To investigate the application potential of alginate-strontium (Sr) hydrogel as an injectable scaffold material in bone tissue engineering. Methods The alginate-Sr/-calcium (Ca) hydrogel beads were fabricated by adding 2.0wt% alginate sodium to 0.2 mol/L SrCl2/CaCl2 solution dropwise. Microstructure, modulus of compression, swelling rate, and degradability of alginate-Sr/-Ca hydrogels were tested. Bone marrow mesenchymal stem cells (BMSCs) were isolated from femoral bones of rabbits by flushing of marrow cavity. BMSCs at passage 5 were seeded onto the alginate-Sr hydrogel (experimental group) and alginate-Ca hydrogel (control group), and the viability and proliferation of BMSCs in 2 alginate hydrogels were assessed. The osteogenic differentiation of cells embeded in 2 alginate hydrogels was evaluated by alkaline phosphate (ALP) activity, osteoblast specific gene [Osterix (OSX), collagen type I, and Runx2] expression level and calcium deposition by fluorescent quantitative RT-PCR and alizarin red staining, Von Kossa staining. The BMSCs which were embeded in alginate-Ca hydrogel and cultured with common growth medium were harvested as blank control group. Results The micromorphology of alginate-Sr hydrogel was similar to that of the alginate-Ca hydrogel, with homogeneous pore structure; the modulus of compression of alginate-Sr hydrogel and alginate-Ca hydrogel was (186.53 ± 8.37) and (152.14 ± 7.45) kPa respectively, showing significant difference (t=6.853, P=0.002); there was no significant difference (t=0.737, P=0.502) in swelling rate between alginate-Sr hydrogel (14.32% ± 1.53%) and alginate-Ca hydrogel (15.25% ± 1.64%). The degradabilities of 2 alginate hydrogels were good; the degradation rate of alginate-Sr hydrogel was significantly lower than that of alginate-Ca hydrogel on the 20th, 25th, and 30th days (P lt; 0.05). At 1-4 days, the morphology of cells on 2 alginate hydrogels was spherical and then the shape was spindle or stellate. When three-dimensional cultured for 21 days, the DNA content of BMSCs in experimental group [(4.38 ± 0.24) g] was significantly higher than that in control group [(3.25 ± 0.21) g ] (t=8.108, P=0.001). On the 12th day after osteogenic differentiation, the ALP activity in experimental group was (15.28 ± 1.26) U/L, which was significantly higher than that in control group [(12.07 ± 1.12) U/L] (P lt; 0.05). Likewise, the mRNA expressions of OSX, collagen type I, and Runx2 in experimental group were significantly higher than those in control group (P lt; 0.05). On the 21th day after osteogenic differentiation, alizarin red staining and Von Kossa staining showed calcium deposition in 2 groups; the calcium nodules and phosphate deposition in experimental group were significantly higher than those in control group (P lt; 0.05). Conclusion Alginate-Sr hydrogel has good physicochemical properties and can promote the proliferation and osteogenic differentiation of BMSCs, so it is an excellent injectable scaffold material for bone tissue engineering.
Objective To review new progress of related research of bone tissue engineering in recent years. Methods Domestic and international l iterature concerning bone tissue engineering was reviewed and analyzed. Results In the recent years, great progression had been made in the research and development of bone tissue engineering, it had been used in more and more hospitals, and relevant national regulations and protocols had been set up. As to seed cells of bone tissue engineering, autologous and allogeneic stem cells had been widely used, while recently embryonic stem cells and induced pluri potent stem cells had attracted most attentions. In the field of scaffolds materials, significant improvementshad been made, from natural extractions to artificial polymers; from single construction to multiple compounds with surface modifications. As to the methods of construction, the static seeding approach had been widely accepted, and the appl ications of bioreactor had provided a stable and various micro-enviroment for the vitro-culture of different stem cells, which had beenregarded as an alternative way of vitro-culture and construction for bone tissue engineering. Conclusion With the tremendous help of the techniques and approaches above, we shall expect a promising future of a new generation bone tissue engineering based medical products in the years to come.
ObjectiveTo evaluate the effect of tissue engineered periosteum on the repair of large diaphysis defect in rabbit radius, and the effect of deproteinized bone (DPB) as supporting scaffolds of tissue engineering periosteum. MethodsBone marrow mesenchymal stem cells (BMSCs) were cultured from 1-month-old New Zealand Rabbit and osteogenetically induced into osteoblasts. Porcine small intestinal submucosa (SIS) scaffold was produced by decellular and a series mechanical and physiochemical procedures. Then tissue engineered periosteum was constructed by combining osteogenic BMSCs and SIS, and then the adhesion of cells to scaffolds was observed by scanning electron microscope (SEM). Fresh allogeneic bone was drilled and deproteinized as DPB scaffold. Tissue engineered periosteum/DPB complex was constructed by tissue engineered periosteum and DPB. Tissue engineered periosteum was "coat-like" package the DPB, and bundled with absorbable sutures. Forty-eight New Zealand white rabbits (4-month-old) were randomly divided into 4 groups (groups A, B, C, and D, n=12). The bone defect model of 3.5 cm in length in the left radius was created. Defect was repaired with tissue engineered periosteum in group A, with DPB in group B, with tissue engineered periosteum/DPB in group C; defect was untreated in group D. At 4, 8, and 12 weeks after operation, 4 rabbits in each group were observed by X-ray. At 8 weeks after operation, 4 rabbits of each group were randomly sacrificed for histological examination. ResultsSEM observation showed that abundant seeding cells adhered to tissue engineered periosteum. At 4, 8, and 12 weeks after operation, X-ray films showed the newly formed bone was much more in groups A and C than groups B and D. The X-ray film score were significantly higher in groups A and C than in groups B and D, in group A than in group C, and in group B than in group D (P<0.05). Histological staining indicated that there was a lot of newly formed bone in the defect space in group A, with abundant newly formed vessels and medullary cavity. While in group B, the defect space filled with the DPB, the degradation of DPB was not obvious. In group C, there was a lot of newly formed bone in the defect space, island-like DPB and obvious DPB degradation were seen in newly formed bone. In group D, the defect space only replaced by some connective tissue. ConclusionTissue engineered periosteum constructed by SIS and BMSCs has the feasibility to repair the large diaphysis defect in rabbit. DPB isn't an ideal support scaffold of tissue engineering periosteum, the supporting scaffolds of tissue engineered periosteum need further exploration.