OBJECTIVE: To study the feasibility of calcium polyphosphate fiber (CPPF) as the scaffold material of tendon tissue engineering. METHODS: CPPF (15 microns in diameter) were woven to form pigtail of 3 mm x 2 mm transverse area; and the tensile strength, porous ratio and permeability ratio were evaluated in vitro. Tendon cells (5 x 10(4)/ml) derived from phalangeal flexor tendon of SD rats were co-culture with CPPF scaffold or CPPF scaffold resurfaced with collagen type-I within 1 week. The co-cultured specimens were examined under optical and electric scanning microscope. RESULTS: The tensile strength of CPPF scaffolds was (122.80 +/- 17.34) N; permeability ratio was 61.56% +/- 14.57%; and porous ratio was 50.29% +/- 8.16%. CPPF had no obvious adhesive interaction with tendon cells, while CPPF of surface modified with collagen type-I showed good adhesive interaction with tendon cells. CONCLUSION: The above results show that CPPF has some good physical characteristics as scaffold of tendon tissue engineering, but its surface should be modified with organic substance or even bioactive factors.
OBJECTIVE: To study chondrogenesis of calcium alginate-chondrocytes predetermined shapes. METHODS: Chondrocytes isolated from ears of rabbit by type II collagenase digestion, and then were mixed with 1.5% solidium alginate solution. The suspension was gelled to create three spatial shapes as triangle, circle and quadrilateral by immersed into 2.5% CaCl2 for 90 minutes, and then was implanted into the subcutaneous pocket on the dorsum of the rabbit. Samples were harvested at 6 and 12 weeks after implantation. RESULTS: Gross examination of excised specimens at 6 and 12 weeks after implantation revealed the presence of new cartilage of approximately the same dimensions as the original construct. Histologic evaluation using hematoxylin and eosin stains confirmed the presence of cartilage nodules at 6 weeks after implantation. After 12 weeks, mature cartilage was observed and histologic analysis confirmed the presence of well formed cartilaginous matrix. CONCLUSION: Predetermined shapes neocartilage can be regenerated using calcium alginate as a carrier of chondrocytes in the bodies of immune animals.
【Abstract】Objective To investigate the protective effect of improving the pancreatic ischemia and calcium channel blockers on preventing the progression of acute pancreatitis. Methods Twenty-four patients with mild acute pancreatitis were randomly divided into two groups： control group and treated group. Within the first 72 hours from the onset of AP, routine conservative managements were performed in control group, improving the pancreatic ischemia and preventing Ca2+ overload were performed in treated group for two weeks. The hemorrheological parameters were measured at 1,4,7,14 days after adimission, simultanously, serum TNFα, IL-1β, C-reactive protein and plasma TXB2, 6-keto-PGF1α levels were determined with ELISA methods. Results The hemorrheological changes were improved in treated group, serum TNFα, IL-1β, C-reactive protein and plasma TXB2, 6-keto-PGF1α levels were significantly decreased each time point in treated group as compared with control group. Conclusion Improving the pancreatic ischemia and calcium channel blockers have protective effect through reducing the generation of cytokines and inflammatory mediators on preventing the progression of acute pancreatitis.
Objective To investigate the biomechanics of a novel injectable calcium phosphate cement (CPC) composited by poly (lactic-co-glycolic acid) (PLGA) combined with double-screw fixation in repairing Schatzker II type tibial plateau fracture, so as to provide the mechanical basis for the clinical minimally invasive treatment. Methods Ten matched pairs of proximal tibia specimens were harvested from 10 elderly cadavers to prepare Schatzker II type tibial plateau fracture model. Fracture was fixed by forcing injection of CPC (experimental group) or autologous cancellous bone (control group) combined with double-screw fixation. The samples underwent axial compression on MTS 858 material testing machine to measure the load-displacement, the maximum load, and compressive stiffness. Results The novel CPC had good injectable property at room temperature, which could fill in bone defect fully and permeated into the surrounding cancellous bone. The average bone mineral density of tibial metaphysis was (0.639 ± 0.081) g/cm2 in the experimental group and (0.668 ± 0.083) g/ cm2 in the control group, showing no significant difference (t=1.012, P=0.331). The maximum load in the experimental group [(4 101 ± 813) N] was significantly higher than that in the control group [(692 ± 138) N] (t=3.932, P=0.001). The compressive stiffness was (1 363 ± 362) N/mm in the experimental group and was (223 ± 54) N/mm in the control group, showing significant difference (t=3.023, P=0.013). Conclusion The novel CPC can effectively restore the biomechanical properties of tibilal plateau in repairing Schatzker II type tibial plateau fracture by means of forcing injection combining with double-screw fixation. It could be used as an effective bone substitute in the clinical application.
Objective To investigate the role of calcium- and integrin-binding protein-1（CIB1） in oxidized lowdensity lipoprotein（OX-LDL） inhibiting migration of mouse macrophages. Methods To silence CIB1 express of mouse macrophages by RNA interference, then incubating mouse macrophages with OX-LDL, cell migration and cell spreading of mouse macrophages were analyzed. Results At 24-72h after macrophages transfected CIB1 siRNA, the express of CIB1 protein was restrained obviously. To silence CIB1 express could increase migration and spreading of mouse macrophages significantly. Conclusions CIB1 plays the important role in intracellular modulating mechanism of OX-LDL inhibiting mouse macrophages migration.
Purpose To examine the change of optic disc blood flow in primary open angle glaucoma(POAG) patients after cold provocation test and nifedipine administration． Methods Using Heidelberg retinal flowmetry (HRF),the blood flow of optic disc of glaucoma patients and normal control subjects were measured under basal condition, after cold provocation test,and after nifedipine administration. Results The mean optic disc blood volume and flow of POAG patients reduced from 27.1 and 545.4 to 22.3 and 452.4 after cold provocation test (Plt;0.05),and increased to 29.0 and 579.5 after nifedipine adminstration(Plt;0.05).The changes of mean optic disc blood flow of patients with a history of cold extremities show statistic significance compared with whom without such history (Plt;0.05)). Conclusion The changes of blood flow of optic disc in POAG patients may be influenced by cold stimuli and administration of nifedipine,and the history of cold extremities might be connected with the change of optic disc blood flow in POAG patients. (Chin J Ocul Fundus Dis,2000,16:85-87)
Objective To investigate the in vivo degradable properties of new calcium phosphate cement (CPC) containing poly lactic-co-glycolic acid (PLGA) so as to lay a foundation for the future clinical application. Methods A novel CPC containing PLGA (CPC/PLGA) was prepared according to a ratio of 45% dicalcium phosphate anhydrous ∶ 45% partially crystallized calcium phosphates ∶ 10% PLGA. Thirty-two adult New Zealand rabbits (weighing 2.2-3.0 kg, male or female in half) were divided into the experimental group (n=17) and the control group (n=15). The bone defect models of the bilateral femoral condyles (4.5 mm in diameter and 1.5 cm in depth) were made by drilling hole. Defect at the right side was repaired with CPC/ PLGA in the experimental group and with CPC in the control group, while defect at the left side was not treated as blank control. The general condition of rabbits was observed after operation; the histological observation and bone histomorphometric analysis were performed at 2, 4, 8, 16, and 24 weeks; and scanning electronic microscope (SEM) observation was performed at 8 and 16 weeks after operation. Results All rabbits survived to the end of experiment. The histological observation showed: CPC/PLGA degraded gradually, and the new-born bone trabecula ingrew; bone trabeculae became rough and b; and CPC/PLGA almost biodegraded at 24 weeks in the experimental group. The CPC degradation was much slower in the control group than in the experimental group. The total bone tissue percentage was 44.9% ± 23.7% in the experimental group, and 25.7% ± 10.9% in the control group, showing significant difference between 2 groups (t=3.302, P=0.001); and the bone tissue percentage showed significant difference between 2 groups at 8, 16, and 24 weeks (P lt; 0.05). The results of SEM observation showed that the pore size was 100-300 μm at 8 weeks after operation, new-born bone trabecula grew into the pores and combined bly with residual cement in the experimental group. Conclusion Novel CPC/PLGA has good in vivo degradable properties, and it can be an ideal bone substitute in future clinical application.
ObjectiveTo investigate the short-term effectiveness of balloon vertebroplasty combined with short-segment pedicle screw instrumentation for the treatment of thoracolumbar burst fractures. MethodsBetween June 2011 and December 2013, 22 patients with thoracolumbar burst fractures were included. There were 14 males and 8 females, aged 20-60 years (mean, 42.5 years). The fracture segments included T11 in 1 case, T12 in 4 cases, L1 in 10 cases, L2 in 6 cases, and L3 in 1 case. According to AO classification system, there were 13 cases of type A and 9 cases of type B. Spinal cord injury was classified as grade C in 2 cases, grade D in 3 cases, and grade E in 17 cases according to Frankel scale. The time from injury to operation was 3-10 days (mean, 5.5 days). All patients underwent posterior reduction and fixation via the injured vertebra, transpedicular balloon reduction of the endplate and calcium sulfate cement (CSC) injection. The ratio of anterior vertebral height, the ratio of central vertebral height, the sagittal Cobb angle, the restoration of nervous function, and internal fixation failure were analyzed. ResultsPrimary healing of incision was obtained in the others except 2 cases of poor healing, which was cured after dressing change or debridement. All the patients were followed up 9-40 months (mean, 15 months). CSC leakage occurred in 2 cases. Absorption of CSC was observed at 8 weeks after operation with complete absorption time of 12-16 weeks (mean, 13.2 weeks). The mean fracture healing time was 18.5 weeks (range, 16-20 weeks). The ratio of anterior vertebral height, ratio of central vertebral height, and sagittal Cobb angle were significantly improved at 1 week and 3 months after operation and last follow-up when compared with preoperative values (P<0.01), but no significant difference was found among 3 time points after operation (P>0.01). There was no internal fixation failure or Cobb angle loss more than 10°. Frankel scale was improved with no deterioration of neurologic function injury. ConclusionBalloon vertebroplasty combined with short-segment pedicle screw instrumentation is simple and safe for the treatment of thoracolumbar burst fractures, and it can improve the quality of reduction, restore vertebral mechanical performance effectively, and prevent the loss of correction and internal fixation failure.
Objective To probe the change of the structure and function of the small bowel by injection of different drugs (verapamil, energy compounds or normal saline) via the superior mesenteric artery (SMA) injections.Methods The model of the small intestine ischemia/reperfusion (I/R) injury was made in grey rabbits. Free calcium concentration in mitochondria of the small intestine was determined, and the ultrastructural change was also observed by electron microscopy at the very time of occlusion, 60 minutes after occlusion and 30 minutes after reperfusion. Results The free calcium concentration in mitochondria was more declined in verapamil group (2.976±0.410 nmol/mg.prot) than in N.S. group (4.234±0.542 nmol/mg.prot), Ｐ＜0.01, at 60 minutes after occlusion. At 30 minutes after reperfusion, free calcium concentration in mitochondria was more decreased in energy compunds group (2.401±0.323 nmol/mg.prot) and verapamil group (3.847±0.610 nmol/mg.prot) than in the N.S. group (5.981±1.031 nmol/mg.prot). Conclusion Verapamil and energy compouds have protective effects on the functions and ultrastructures of the I/R of small intestine.
Free calcium ions, as a kind of message-transport substance, is important in cellular activity such as cell movement, cell differentiation and cell proliferation. In order to investigate the relationship between free calcium ions and scar contracture, the fibroblasts which originated from hypertrophic scar, keloid and normal skin were used as the experimental target. The fibroblasts from 4th-6th generations of different sources were used; Then the intracellular free calcium ions concentrations were measured respectively by the fluorescent Ca2+ indicator Fura-2/AM and Image analysis system. The results showed that the level of Ca2+ in fibroblasts of hypertrophic scar was higher than that in keloid and normal skin (P lt; 0.01). There was no significant difference between the level of Ca2+ in keloid and in normal skin. The conclusion was that the concentration of intracellular free calcium ions played an important role in the scar contract, but the exact mechanism was still unclear and required further study.