【Abstract】 Objective To develop a novel cartilage acellular matrix (CACM) scaffold and to investigate its performance for cartilage tissue engineering. Methods Human cartilage microfilaments about 100 nm-5 μm were prepared after pulverization and gradient centrifugation and made into 3% suspension after acellularization treatment. After placing the suspension into moulds, 3-D porous CACM scaffolds were fabricated using a simple freeze-drying method. The scaffolds were cross-l inked by exposure to ultraviolet radiation and immersion in a carbodiimide solution 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide hydrochloride and N-hydroxysucinimide. The scaffolds were investigated by histological staining, SEM observation and porosity measurement, water absorption rate analysis. MTT test was also done to assess cytotoxicity of the scaffolds. After induced by conditioned medium including TGF-β1, canine BMSCs were seeded into the scaffold. Cell prol iferation and differentiation were analyzed using inverted microscope and SEM. Results The histological staining showed that there are no chondrocytefragments in the scaffolds and that toluidine blue, safranin O and anti-collagen II immunohistochemistry staining werepositive. The novel 3-D porous CACM scaffold had good pore interconnectivity with pore diameter (155 ± 34) μm, 91.3% ± 2.0% porosity and 2 451% ± 155% water absorption rate. The intrinsic cytotoxicity assessment of novel scaffolds using MTT test showed that the scaffolds had no cytotoxic effect on BMSCs. Inverted microscope showed that most of the cells attached to the scaffold. SEM micrographs indicated that cells covered the scaffolds uniformly and majority of the cells showed the round or ell iptic morphology with much matrix secretion. Conclusion The 3-D porous CACM scaffold reserved most of extracellular matrix after thoroughly decellularization, has good pore diameter and porosity, non-toxicity and good biocompatibil ity, which make it a suitable candidate as an alternative cell-carrier for cartilage tissue engineering.
Objective To investigate the effect of collagen type I concentration on the physical and chemical properties of the collagen hydrogel, and to analyze the effect of different concentrations of collagen type I hydrogel on the phenotype and gene expression of the chondrocytes in vitro. Methods Three kinds of collagen hydrogels with concentrations of 12, 8, and 6 mg/ mL (C12, C8, and C6) were prepared, respectively. The micro-structure, compressive modulus, and swelling ratio of the hydrogels were measured and analyzed. The chondrocytes at 2nd passage were cocultured with three kinds of collagen hydrogels in vitro, respectively. After 1-day culture, the samples were stained with fluorescein diacetate (FDA) / propidium iodide (PI) and the cell activity was observed under confocal laser microscope. After 14-day culture, HE staining and toluidine blue staining were carried out to observe the histological morphology, and mRNA expressions of chondrocytes related genes (collagen type II, Aggrecan, collagen type I, collagen type X, Sox9) were determined by real-time fluorescent quantitative PCR. Results With the increase of collagen type I concentration from 6 to 12 mg/mL, the physical and chemical properties of the collagen hydrogels changed significantly: the fiber network became dense; the swelling ratios of C6, C8, and C12 were 0.260 ± 0.055, 0.358 ± 0.072, and 0.539 ± 0.033 at 192 hours, respectively, showing significant differences among 3 groups (P lt; 0.05); and the compression modulus were (4.86 ± 0.96), (7.09 ± 2.33), and (11.08 ± 3.18) kPa, respectively, showing significant differences among 3 groups (P lt; 0.05). After stained with FDA/PI, most cells were stained green, and few were stained red. The histological observation results showed that the chondrocytes in C12 hydrogels aggregated obviously with b heterochromia, chondrocytes in C8 hydrogels aggregated partly with obvious heterochromia, and chondrcytes in C6 hydrogels uniformly distributed with weak heterochromia. Real-time fluorescent quantitative PCR results showed that the mRNA expressions of collagen type II and Aggrecan were at the same level in C12, C8, and C6; the expressions of collagen type I, Sox9, and collagen type X were up-regulated with the increase of collagen type I hydrogels concentration, and the expressions were the highest at 12 mg/mL and were the lowest at 6 mg/mL, showing significant differences among 3 groups (P lt; 0.05). Conclusion Increasing the concentration of collagen hydrogels leads to better mechanical properties and higher shrink-resistance, but it may induce the up-regulation of cartilage fibrosis and hypertrophy related gene expression.
Objective To review the research progress of articular cartilage scaffold materials and look into the future development prospects. Methods Recent literature about articular cartilage scaffold for tissue engineering was reviewed, and the results from experiments and clinical application about natural and synthetic scaffold materials were analyzed. Results The design of articular cartilage scaffold for tissue engineering is vital to articular cartilage defects repair. The ideal scaffold can promote the progress of the cartilage repair, but the scaffold materials still have their limitations. Conclusion It is necessary to pay more attention to the research of the articular cartilage scaffold, which is significant to the repair of cartilage defects in the future.
Objective To elucidate the latest research progress and application of tissue engineered meniscus. Methods The literature concerning the advance in tissue engineered meniscus was extensively reviewed, then closely-related issues including seed cells, scaffolds, and bioreactors were analyzed. Results With more and more attention being paid to meniscus tissue engineering, different approaches and strategies for seed cells, scaffolds, and bioreactors have contributed to the generation of meniscal constructs, which are capable of restoring meniscal lesions to some extent, but translating successes in basic science research to clinical application is still limited. Conclusion More research for the optimal combination of the appropriate cell source, the scaffold type, and the proper physical and chemical factors for the stimulation of cells differentiation into tissue with optimal phenotypes in tissue engineered meniscus is still in needed, but the overall future looks promising.
Objective To review the latest development in the research on the application of the electrostatic spinning technology in preparation of the nanometer high polymer scaffold. Methods The related articles published at home and abroad during the recent years were extensively reviewed and comprehensively analyzed. Results Micro/nano-structure and space topology on the surfaces of the scaffold materials, especially the weaving structure, were considered to have an important effect on the cell adhesion, proliferation, directional growth, and biological activation. The electrospun scaffold was reported to have a resemblance to the structure of the extracellular matrix and could be used as a promising scaffold for the tissue engineeringapplication. The electrospun scaffolds were applied to the cartilage, bone, blood vessel, heart, and nerve tissue engineering fields. Conclusion The nanostructured polymer scaffold can support the cell adhesion, proliferation, location, and differentiation，and this kind of scaffold has a considerable value in the tissue engineering field.
ObjectiveTo investigate the influences of lactic acid (LA), the final degradation product of polylactic acid (PLA) on the prol iferation and osteoblastic phenotype of osteoblast-l ike cells so as to provide theoretical basis for bone tissue engineering. MethodsRos17/2.8 osteoblast-l ike cells were harvested and divided into 3 groups. In groups A and B, the cells were cultured with the medium containing 4, 8, 16, 22, and 27 mmol/L L-LA and D, L-LA, respectively. In group C, the cells were cultured with normal medium (pH7.4). The cell prol iferation was determined with MTT method after 1, 3, and 5 days. The relative growth ratio (RGR) was calculated, and the cytotoxicity was evaluated according to national standard of China. In addition, the alkal ine phosphatase (ALP) activity of cells cultured with medium containing 4 mmol/L L-LA (group A), 4 mmol/ L D, L-LA (group B), and normal medium (group C) after 1 and 5 days were detected with ALP kits, and the relative ALP ratio (RAR) was calculated; after 21 days, the calcium nodules were tested with von Kossa staining method, and were quantitatively analyzed. ResultsWhen LA concentration was 4 mmol/L, the mean RGR of both groups A and B were all above 80%, and the cytotoxic grades were grade 0 or 1, which meant non-cytotoxicity. When LA concentration was 8 mmol/L and 16 mmol/ L, groups A and B showed cytotoxicity after 5 days and 3 days, respectively. When LA concentration was above 22 mmol/L, cell prol iferations of groups A and B were inhibited evidently after 1-day culture. At each LA concentration, RGR of group A was significantly higher than that of group B at the same culture time (P<0.05) except those at 4 mmol/L after 1-day and 3-day culture. After 1 day, the RAR of group A was significantly higher than that of group B on 1 day (144.1%±3.2% vs. 115.2%±9.8%, P<0.05) and on 5 days (129.6%±9.8% vs. 78.2%±6.9%, P<0.05). The results of von Kossa staining showed that the black gobbets in group A were obviously more than those of groups B and C. The staining area of group A (91.2%±8.2%) was significantly higher than that of groups B (50.3%±7.9%) and C (54.2%±8.6%) (P<0.05). ConclusionThe concentration and composition of LA have significant effects on the cell proliferation and osteoblastic phenotype of osteoblast-l ike cells.
Objective To explore a novel nanometer biomaterial which could induce the regeneration of tooth tissues intell igently, and to evaluate the feasibil ity of using this kind of biomaterial as the scaffold for tooth tissue engineering by investigating the role it plays in tooth tissue engineering. Methods The scaffold for tooth tissue engineering containing recombinant human bone morphogenetic protein 2 (rhBMP-2) was prepared by mixing nanoscale β tricalcium phosphate (β-TCP)/collagen particles. Forty-six 8-10 weeks old specific pathogen free Sprague Dawley (SD)rats, including 34 females and 12 males, weighing 250-300 g, were involved in this study. Tooth germs were removed under a stereomicroscope from the mandible of newborn SD rat, then digested and suspended. Scanning electronic microscope (SEM), adhesion rate of cells, and MTT assay were used to evaluate the effects of the scaffold on the tooth germ cells cultured in vitro. The tissue engineered tooth germ which was constructed by tooth germ cells and scaffold was transplanted under SD rat’s kidney capsule as the experimental group (n=12); the tooth germ cells (cell-control group, n=12) or scaffold without cells (material-control group, n=4) were transplanted separately as control groups Specimens were harvested to perform general and histological observations at 4 and 8 weeks after transplantation. Results β-TCP/collagen showed a loose and porous appearance with soft texture and excellent hydrophil icity. Tooth germ cells grew well and could attach to the scaffold tightly 3 days after coculture. The adhesion rates of tooth germ cells were 27.20% ± 2.37%, 44.52% ± 1.87%, and 73.81% ± 4.15% when cocultured with scaffold for 4, 8, and 12 hours, respectively. MTT assay showed that the cell prol iferation status of experimental group was similar to that of the control group, showing no significant difference (P gt; 0.05). Some white calcified specimens could be harvested at 4-8 weeks after transplantation. At 4 weeks after transplantation some typical structures of dental cusp and enamel-dentin l ike tissues could be seen in the experimental group. Enamel-dentin l ike tissues also formed in some specimens of cell-control group, but they arranged irregularly. At 8 weeks after transplantation the enamel-dentin l ike tissue of experimental group exhibited a mature appearance and organized structure in comparison with that at 4 weeks. And mature enamel or dentin l ike tissue also could be seen in cell-control group. In contrast, there was no enamel or dentin l ike tissue in material-control group at 4 or 8 weeks after transplantation. Conclusion rhBMP-2 decorated β-TCP/collagen scaffold has good biocompatibil ity and can be used as a novel nanometer biomaterial, so it is a good choice in scaffolds for tooth tissue engineering.
Objective To investigate the feasibil ity of using thermo-sensitive chitosan hydrogen as a scaffold to construct tissue engineered injectable nucleus pulposus (NP). Methods Three-month-old neonatal New Zealand rabbits (male or female) weighing 150-200 g were selected to isolate and culture NP cells. The thermo-sensitive chitosan hydrogel scaffold wasmade of chitosan, disodium β-glycerophosphate and hydroxyethyl cellulose. Its physical properties and gross condition were observed. The tissue engineered NP was constructed by compounding the scaffold and rabbit NP cells. Then, the viabil ity of NP cells in the chitosan hydrogel was observed 2 days after compound culture and the growth condition of NP cells on the scaffold was observed by SEM 7 days after compound culture. NP cells went through histology and immunohistochemistry detection and their secretion of aggrecan and expression of Col II mRNA were analyzed by RT-PCR 21 days after compound culture. Results The thermo-sensitive chitosan hydrogel was l iquid at room temperature and sol idified into gel at 37 (15 minutes) due to crossl inking reaction. Acridine orange-propidiumiodide staining showed that the viabil ity rate of NP cells in chitosan hydrogel was above 90%. Scanning electron microscope observation demonstrated that the NP cells were distributed in the reticulate scaffold, with ECM on their surfaces. The results of HE, toluidine blue, safranin O and histology and immunohistochemistry staining confirmed that the NP cells in chitosan hydrogel were capable of producing ECM. RT-PCR results showed that the secretion of Col II and aggrecan mRNA in NP cells cultured three-dimensionally by chitosan hydrogen scaffold were 0.631 ± 0.064 and 0.832 ± 0.052, respectively,showing more strengths of producing matrix than that of monolayer culture (0.528 ± 0.039, 0.773 ± 0.046) with a significant difference (P lt; 0.05). Conclusion With good cellular compatibilities, the thermo-sensitive chitosan hydrogel makes it possible for NP cells to maintain their normal morphology and secretion after compound culture, and may be a potential NP cells carrier for tissue engineered NP.
Objective To study the mechanism of ectopic osteogenesis of nacre/Polylactic acid (N/P) artificial bone combined with allogenic osteoblasts, and to explore the possibility as a scaffold material of bone tissue engineering. Methods The allogenic- osteoblasts seeded onto N/P artificial bone were co-cultured in vivo 1 week.The N/P artificial bone with allogenic osteoblasts were implanted subcutaneously into the left back sites of the New Zealand white rabbits in the experimental group and the simple N/P artificial bone into the right ones in the control group. The complexes were harvested and examined by gross observation, histologic analysis and immunohistochemical investigation 2, 4 and 8 weeks after implantation respectively.Results In experimental group, the osteoid formed after 4 weeks, and the mature bone tissue withbone medullary cavities formed after 8 weeks; but in control group there was nonew bone formation instead of abundant fibrous tissue after 4 weeks, and more fibrous tissue after 8 weeks.Conclusion N/P artificial bone can be used as an optical scaffold material of bone tissue engineering.
Objective To investigate the biocompatibil ity of silk fibroin nanofibers scaffold with olfactory ensheathing cells (OECs) and to provide an ideal tissue engineered scaffold for the repair of spinal cord injury (SCI). Methods Silk fibroin nanofibers were prepared using electrospinning techniques and were observed by scanning electron microscope (SEM). Freshly isolated OECs from SD rats purified by the modified differential adherent velocity method were cultured. The cells at passage 1 (1 × 104 cells/cm2) were seeded on the poly-l-lysine (control group) and the silk fibroin nanofibers (experimental group) coated coversl ips in Petri dish. At desired time points, the morphological features, growth,and adhesion of the cells were observed using phase contrast inverted microscopy. The OECs were identified by the nerve growth factor receptor p75 (NGFR p75) immunofluorescence staining. The viabil ity of OECs was examined by l ive/dead assay. The prol iferation of OECs was examined by MTT assay. The cytotoxicity of the nanofibers was evaluated. Results The SEM micrographs showed that the nanofibers had a smooth surface with sol id voids among the fibers, interconnecting a porous network, constituted a fibriform three dimensional structure and the average diameter of the fibers was about (260 ± 84) nm. The morphology of OECs on the experimental group was similar to the cell morphology on the control group, the cells distributed along the fibers, and the directions of the cell protrusions were in the same as that of the fibers. Fluorescence microscopy showed that the purity of OECs was 74.21% ± 2.48% in the experimental group and 79.05% ± 2.52% in the control group 5 days after culture. There was no significant difference on cell purity between two groups (P gt; 0.05). The OECs in the experimental group stained positive for NGFR p75 compared to the control group, indicating that the cells in the experimental group still maintained the OECs characteristic phenotype. Live/dead staining showed that high viabil ity was observed in both groups 3 days after culture. There was no significant difference on cell viabil ity between two groups. The prol iferation activity at 1, 3, 5, 7, and 10 days was examined by MTT assay. The absorbency values of the control group and the experimental group had significant differences 3 and 5 days after culture (P lt; 0.05). The relative growth rates were 95.11%, 90.35%, 92.63%, 94.12%, and 94.81%. The cytotoxicity of the material was grade 1 and nonvenomous according to GB/T 16886 standard. Conclusion Silk fibroin nanofibers scaffold has good compatibility with OECs and is a promising tissue engineered scaffold for the repair of SCI.