【Abstract】 Objective To develop a novel cartilage acellular matrix (CACM) scaffold and to investigate its performance for cartilage tissue engineering. Methods Human cartilage microfilaments about 100 nm-5 μm were prepared after pulverization and gradient centrifugation and made into 3% suspension after acellularization treatment. After placing the suspension into moulds, 3-D porous CACM scaffolds were fabricated using a simple freeze-drying method. The scaffolds were cross-l inked by exposure to ultraviolet radiation and immersion in a carbodiimide solution 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide hydrochloride and N-hydroxysucinimide. The scaffolds were investigated by histological staining, SEM observation and porosity measurement, water absorption rate analysis. MTT test was also done to assess cytotoxicity of the scaffolds. After induced by conditioned medium including TGF-β1, canine BMSCs were seeded into the scaffold. Cell prol iferation and differentiation were analyzed using inverted microscope and SEM. Results The histological staining showed that there are no chondrocytefragments in the scaffolds and that toluidine blue, safranin O and anti-collagen II immunohistochemistry staining werepositive. The novel 3-D porous CACM scaffold had good pore interconnectivity with pore diameter (155 ± 34) μm, 91.3% ± 2.0% porosity and 2 451% ± 155% water absorption rate. The intrinsic cytotoxicity assessment of novel scaffolds using MTT test showed that the scaffolds had no cytotoxic effect on BMSCs. Inverted microscope showed that most of the cells attached to the scaffold. SEM micrographs indicated that cells covered the scaffolds uniformly and majority of the cells showed the round or ell iptic morphology with much matrix secretion. Conclusion The 3-D porous CACM scaffold reserved most of extracellular matrix after thoroughly decellularization, has good pore diameter and porosity, non-toxicity and good biocompatibil ity, which make it a suitable candidate as an alternative cell-carrier for cartilage tissue engineering.
Objective To explore an experimental method of transfecting the marrow stromal stem cells (MSCs) with the reconstructed PGL3-t ransforming growth factor-β1 (TGF-β1) gene and to evaluate the feasibility of selfinduction of MSCs to the chondrocytes in vitro so as to provide a scientific and experimental basis for a further “gene enhanced tissue engineering” research. Methods The rabbit MSCs was transfected with the reconstructed PGL3-TGF-β1gene by the Liposo mesMethod, the growth of the cells were observed, and the growth curve was drawn. The living activity of the transfected cells in the experimental group was evalua ted by MTT, and the result was significantly different when compared with that in the control group. By the immunohistochemistry method (SABC), the antigens of TGF-β1 and collagen Ⅱ were examined at 2 and 7 days of the cell culture afte r transfe ction with PGL3-TGF-β1gene. The pictures of the immunohistochemistry slice were analyzed with the analysis instrument, and the statistical analysis was perfor med with the software of the SPSS 11.0, compared with the control group and the blank group. Results Transfection of the cultured rabbit MSCs in vitro with the reconstructed PGL3-TGF-β1gene by the Liposomes Method achie ved a success, with a detection of the Luceraferase activity. The result was significantly different from that in the control group (Plt;0.01). Tested by MTT, the living acti vity of the transfected cells was proved to be significantly decreased (Plt;0.01 vs. the control group). By the immunohistochemistry method (SABC) to study TGF-β1 positive particles were detected in the experimental group，but there were no positive particles in the control and the blank groups. There was a significant difference between the two groups of the experiment and the control group based on the analysis of the ttest (Plt;0.01). By the immunohistochemistry me thod (SABC) to study collagen Ⅱ, there were more positive particles in the transfected cells in t he experimental group than in the control and the blank groups, and there was a significant difference between the experimental group and the two other groups based on the t-test (Plt;0.01). Conclusion Transfection of the rabbit MSCs with the reconstructed PGL3-TGF-β1 gene by the Liposomes Method is successful. There may be some damage to the cells when transfection is performed. The transfecte d BMS cells with PGL3-TGF-β1 gene can express and excrete TGF-β1when cultured in vitro. The transfected MSCs that secret TGF-β1 can be self-induced into the chondrocytes after being infected for 7 days when cultured in vitro.
Objective To explore the effect of tissue engineered cartilage reconstructed by using sodium alginate hydrogel and SIS complex as scaffold material and chondrocyte as seed cell on the repair of full-thickness articular cartilage defects. Methods SIS was prepared by custom-made machine and detergent-enzyme treatment. Full-thickness articularcartilage of loading surface of the humeral head and the femoral condyle obtained from 8 New Zealand white rabbits (2-3weeks old) was used to culture chondrocytes in vitro. Rabbit chondrocytes at passage 4 cultured by conventional multipl ication method were diluted by sodium alginate to (5-7) × 107 cells/mL, and then were coated on SIS to prepare chondrocyte-sodium alginate hydrogel-SIS complex. Forty 6-month-old clean grade New Zealand white rabbits weighing 3.0-3.5 kg were randomized into two groups according to different operative methods (n=20 rabbits per group), and full-thickness cartilage defect model of the unilateral knee joint (right or left) was establ ished in every rabbit. In experimental group, the complex was implanted into the defect layer by layer to construct tissue engineered cartilage, and SIS membrane was coated on the surface to fill the defect completely. While in control group, the cartilage defect was filled by sodium alginate hydrogel and was sutured after being coated with SIS membrane without seeding of chondrocyte. General condition of the rabbits after operation was observed. The rabbits in two groups were killed 1, 3, 5, 7, and 9 months after operation, and underwent gross and histology observation. Results Eight rabbits were excluded due to anesthesia death, wound infection and diarrhea death. Sixteen rabbits per group were included in the experiment, and 3, 3, 3, 3, and 4 rabbits from each group were randomly selected and killed 1, 3, 5, 7, and 9 months after operation, respectively. Gross observation and histology Masson trichrome staining: in the experimental group, SIS on the surface of the implant was fused with the host tissue, and the inferface between them disappeared 1 month after operation; part of the implant was chondrified and the interface between the implant and the host tissue was fused 3 months after operation; the implant turned into fibrocartilage 5 months after operation; fiber arrangement of the cartilage in theimplant was close to that of the host tissue 7 months after operation; cartilage fiber in the implant arranged disorderly andactive cell metabol ism and prol iferation were evident 9 months after operation. While in the control group, no repair of thedefect was observed 9 months after operation. No obvious repair was evident in the defects of the control group within 9months after operation. Histomorphometric evaluation demonstrated that the staining intensity per unit area of the reparative tissue in the defect of the experimental group was significant higher than that of the control group at each time point (P lt; 0.05), the chondrification in the experimental group was increased gradually within 3, 5, and 7 months after operation (P lt; 0.05), and it was decreased 9 months after operation comparing with the value at 7 months after operation (P lt; 0.05). Conclusion Constructed by chondrocyte-sodium alginate hydrogel-SIS in complex with surficial suturing of SIS membrane, the tissue engineered cartilage can in-situ repair cartilage defect, promote the regeneration of cartilage tissue, and is in l ine with physiological repair process of articular cartilage.
Objective To investigate the feasibility of the complex of the fibrin sealant (FS) and the bone marrow mesenchymal stem cells（MSCs） to createanew cartilage in the nude mice by the issue engineering technique. Methods T he MSCs were isolated from healthy humans and were expanded in vitro. And then the MSCs were induced by the defined medium containing the transforming growth factor β1 (TGF-β1), dexamethasone, and ascorbic acid. The biomechanical properties of the chondrocytes were investigated at 7 and 14 days. The MSCs induced for 7days were collected and mixed with FS. Then, the FSMSCs mixture was injectedby a needle into the dorsum of the nude mice in the experimental group. In the tw o control groups, only FS or MSCs were injected respectively. The specimens were harvested at 6 and 12 weeks，and the ability of chondrogenesis in vivo was inve stigated by the gross observation, HE, Alcian Blue staining, and type Ⅱ collagen immunohistochemistry. Results The MSCs changed from a spindlel ike fibroblastic appearance to a polygonal shape when transferred to the defined medium, and couldbe induced to express the chondrocyte matrix. After an injection of the mixture , the cartilage-like tissue mass was formed, and the specimens were harvested from the mass at 6 and 12 weeks in the experimental group. The tissue mass at 6 we eks was smaller and relatively firm in texture, which had a distinct lacuna structure. And glycosaminoglycan (GAG) and Type II Collagen expressions were detecte d. The tissue mass at 12 weeks was bigger, firmer and glossier with the mature c hondrocytes lying in the lacuna structure. The positive Alcian blue and Collagen II immunohistochemistry stainings were ber at 12 weeks than at 6 weeks. But there was no cartilage-like tissue mass formed in the two control groups. Conclusion This study demonstrates that the fibrin sealant and the bone marrow mesenchymal stem cells can be successfully used in a constructing technique for the tissue engineered injectable cartilage.
To study how to repair the cartilage defect according to the principles of tissue engineering with acellular cartilage matrix as scaffold material. Methods The ear cartilage was obtained from a New Zealand white rabbit(weighing 2.4 kg )and then treated by a modified Courtman’s four-step method to produce the acellular cartilage matrix. Eighteen New Zealand white rabbits (aged 6 months, weighing 2.4-2.6 kg) with no sex l imit were divided into three groups. Forevery rabbit, two pieces of ear cartilage measured 1 cm × 1 cm were excised in each ear. Defects were repaired as follows: group A with the combined graft of acellular cartilage matrix and perichondium, group B with acellular cartilage matrix and group C with perichondium. Three animals in each group were killed 4 and 12 weeks postoperatively, respectively. Tissue samples obtained were analyzed with gross observation, hematoxyl in-eosin stain, Safranine O-alcian blue stain and type II collagen messenger RNA in situ hybridization respectively. Results In gross observation, the repaired sites in groups A and B were not change meaningfully in their shape 4 weeks postoperatively; but they felt a bit of thicker and harder 12 weeks postoperatively. In group C two repaired sites formed scabs at 2 weeks and perforated at 5 weeks. In histological observation, there was a sl ight inflammatory reaction surrounding the acellular cartilage matrix 4 weeks after it was implanted in groups A and B. The inflammatory cells were mainly lymphocytes. The perichondrium graft in group C was collapsed in the defects in HE stain. The defect sites were negative for Safranine O-alcian blue stain and type II collagen mRNA in situ hybridization in all groups. At 12 weeks cells were found in the acellular matrix which arranged in irregular manner in group A in HE stain and was positive for Safranine O-alcian blue stain and type II collagen mRNA in site hybridization. In groups B and C, no new cell was found in HE stain and the repaired sites were negative for Safranine O-alcian blue stain and type II collagen mRNA in situ hybridization. Conclusion Acellular
Objective To investigate the effect of “two-phase” tissue engineered cartilage constructed by autologous marrow mesenchymal stem cells(MSCs) and allogeneic bone matrix gelatin(BMG) in repairing articular cartilage defects. Methods Thirty-twoNew Zealand white rabbits were involved in the experiment. “Two-phase” allogeneic BMG scaffold (one side of porous cancellous bone and the other side of cortical bone; 3 mm both in diameter and in thickness) was prepared from iliac bone and limb bone of 5 rabbits by sequentially chemical method. The MSCs wereseparated from 18 New Zealand white rabbits and induced to express chondrocyticphenotype. The chondrocyte precursor cells were seeded onto “two-phase” allogeneic BMG to construct tissue engineering cartilage. Masson’s trichrome staining, PAS staining and scanning electronic microscopic observation were carried out at 1, 3 and 5 weeks. The defects of full thickness articular cartilage(3 mm both in diameter and in depth) were made at both sides of femoral medial condyles in 27 rabbits(including 18 of separated MSCs and the remaining 9). The defects were repaired with the tissue engineered cartilage at the right side (group A, n=18), with BMG at the left side(group B, n=18), and without any implant at both sides in the remaining 9 rabbits as a control( group C, n=18). After 1, 3 and6 months, the 6 specimens of femoral condyles were harvested in 3 groups, respectively. Gross observation, Masson’s trichrome and Alcian blue staining, modified Wakitani scoring and in situ hybridization of collagen type Ⅱ were carried out to assess the repair efficacy of tissue engineered cartilage. Results The “two-phase” BMG consisted of the dense cortical part and the loose cancellous part. In cancellous part, the pore size ranged 100-800 μm, in which the chondrocyte precursor cells being induced from MSCs proliferated and formed the cell-rich cartilaginous part of tissue engineered cartilage. In cortical part, the pore size ranged 10-40 μm, on which the cells arranged in a layer and formed the hard part of subchondral bone. After 1 month of transplantation, the cartilage and subchondral bone were regenerated in group A; during observation, the regenerated cartilage graduallythinned, but defect was repaired and the structure of the articular surface ansubchondral bone was in integrity. In groups B and C, defects were not repaired, the surrounding cartilage of defect was abrased. According to the modified Wakitani scoring, the indexes in group A were significantly higher than those in group B and C(Plt;0.01) except the thickness of cartilage at 6 months. The positive cell rate of in situ hybridization for collagen type Ⅱ in group A was also higher than those in groups B and C(Plt;0.01). Conclusion “Two-phase” allogeneic BMG is a prospective scaffold for tissue engineered cartilage,which combines with autologous chondrocyte precursor cells induced from MSCs toconstruct the tissue engineering cartilage. The tissue engineered cartilage can repair defects of articular cartilage and subchondral bone.
ObjectiveTo explore the clinical application and effectiveness of a personalized tissue engineered cartilage with seed cells derived from ear or nasal septal cartilage and poly-glycolic acid (PGA)/poly-lactic acid (PLA) as scaffold in patients with nasal reconstruction. MethodsBetween March 2014 and October 2015, 4 cases of acquired nasal defects and 1 case of congenital nasal deformity were admitted. The patient with congenital nasal deformity was a 4-year-old boy, and the source of seed cells was nasal septal cartilage. The other 4 patients were 3 males and 1 female, aged 24-33 years, with an average of 28.5 years. They all had multiple nasal subunit defects caused by trauma and the source of seed cells was auricular cartilage. The tissue engineered cartilage framework was constructed in the shape of normal human nasal alar cartilage and L-shaped silicone prosthesis with seed cells from cartilage and PGA-PLA compound biodegradable scaffold. The boy underwent nasal deformity correction and silicone prosthesis implantation in the first stage, and the prosthesis was removed and implanted with tissue engineered cartilage in the second stage; the remaining 4 adult patients all used expanded forehead flaps for nasal reconstruction. All 5 patients underwent 1-4 nasal revisions. The implanted tissue engineered cartilage was observed during the operation and taken from 2 patients for histological examination.ResultsAll the incisions healed by first intention after the tissue engineered cartilage implantation, and the expanded forehead flaps survived. Postoperative low fever occurred in 3 patients. No complications such as infection, obvious immune rejection response, and tissue engineered cartilage protrusion were found in all patients. All patients were followed up 9-74 months (mean, 54.8 months). During follow-up, the patients had no obvious discomfort in the nose and the ventilation function were good. All patients were satisfied with the nasal contour. Early-stage histological examination showed the typical cartilage characteristics in 1 patient after the implantation of tissue engineered cartilage. Late-stage histological examination in 1 patient of tissue engineered cartilage showed the characteristics of fibrous connective tissue; and the other showed there was remaining cartilage.ConclusionThe safety of tissue engineered cartilage constructed in vitro for reconstruction is preliminarily confirmed, but the effectiveness still needs further verification.
ObjectiveTo investigate whether subchondral bone microstructural parameters are related to cartilage repair during large osteochondral defect repairing based on three-dimensional (3-D) printing technique. MethodsBiomimetic biphasic osteochondral composite scaffolds were fabricated by using 3-D printing technique. The right trochlea critical sized defects (4.8 mm in diameter, 7.5 mm in depth) were created in 40 New Zealand white rabbits (aged 6 months, weighing 2.5-3.5 kg). Biomimetic biphasic osteochondral composite scaffolds were implanted into the defects in the experimental group (n=35), and no composite scaffolds implantation served as control group (n=5); the left side had no defect as sham-operation group. Animals of experimental and sham-operation groups were euthanized at 1, 2, 4, 8, 16, 24, and 52 weeks after operation, while animals of control group were sampled at 24 weeks. Subchondral bone microstructural parameters and cartilage repair were quantitatively analyzed using Micro-CT and Wayne scoring system. Correlation analysis and regression analysis were applied to reveal the relationship between subchondral bone parameters and cartilage repair. The subchondral bone parameters included bone volume fraction (BV/TV), bone surface area fraction (BSA/BV), trabecular thickness (Tb.Th), trabecular number (Tb.N), and trabecular spacing (Tb.Sp). ResultsIn the experimental group, articular cartilage repair was significantly improved at 52 weeks postoperatively, which was dominated by hyaline cartilage tissue, and tidal line formed. Wayne scores at 24 and 52 weeks were significantly higher than that at 16 weeks in the experimental group (P<0.05), but no significant difference was found between at 24 and 52 weeks (P>0.05); the scores of experimental group were significantly lower than those of sham-operation group at all time points (P<0.05). In the experimental group, new subchondral bone migrated from the surrounding defect to the centre, and subchondral bony plate formed at 24 and 52 weeks. The microstructural parameters of repaired subchondral bone followed a "twin peaks" like discipline to which BV/TV, BSA/BV, and Tb.N increased at 2 and 16 weeks, and then they returned to normal level. The Tb.Sp showed reversed discipline compared to the former 3 parameters, no significant change was found for Tb.Th during the repair process. Correlation analysis showed that BV/TV, BSA/BV, Tb.Th, Tb.N, and Tb.Sp were all related with gross appearance score and histology score of repaired cartilage. ConclusionSubchondral bone parameters are related with cartilage repair in critical size osteochondral repair in vivo. Microstructural parameters of repaired subchondral bone follow a "twin peaks" like discipline (osteoplasia-remodeling-osteoplasia-remodeling) to achieve reconstruction, 2nd week and 16th week are critical time points for subchondral bone functional restoration.
Objective To evaluate collagen（Col）hyaluronan (HA) chondroitin sulfate (CS) tri-copolymer as a new biomimetic biodegradable polymer scaffold for application of the articular cartilage tissue engineering. Methods The Col-HACS tricopolymer was prepared by freezing and lyophilization and was cross-linked by 1-ethyl-3(3-dimethy inaminoproyl) carbodiimide (EDC). The morpholog icalcharacteristics of the matrices were evaluated by the SME and HE stainings. The rabbit chondrocytes were isolated and seeded in the tricopolymer scaffold. Morphology, proliferation and differentiation of glycosaminoglycan (GAG), and phenotypic expression of the rabbit articular chondrocytes cultured within the tricopolymer scaffold were indicated by the histological examination, SEM, biochemica l analysis, and reverse transcriptase PCR for collagen typeⅡ（ColⅡ）. Results The chondrocytes proliferated and differentiated well, and th ey preserved the phenotypic expression of ColⅡ in the Col-HA-CS scaffold. After the 21day cell culture within the Col-HA-CS scaffolds, the cartilage-specific morphologyand the structural characteristics such as lacunae appeared，and DNA and GAG conten ts increased with the time. In addition, DNA and GAG contents were significantly higher in the Col-HA-CS matrix than in the collagen matrix alone (Plt;0.05 ). Conclusion These results show that the Col-HA-CS tri-copolymer matrices can provide an appropriate environment for the generation of cartilage-like tissues and have a potential application in the cartilage tissue engineering scaffold field.
Objective To investigate the effect of allogeneic chondrocytes-calcium alginate gel composite under the intervention of low intensive pulsed ultrasound (LIPUS) for repairing rabbit articular cartilage defects. Methods Bilateral knee articular cartilage were harvested from 8 2-week-old New Zealand white rabbits to separate the chondrocytes by mechanical-collagen type II enzyme digestion. The 3rd passage chondrocytes were diluted by 1.2% sodium alginate to 5 × 106 cells/mL, then mixed with CaCl2 solution to prepare chondrocytes-calcium alginate gel composite, which was treated with LIPUS for 3 days (F0: 1 MHz; PRF: 1 kHz; Amp: 60 mW/cm2; Cycle: 50; Time: 20 minutes). An articular cartilage defect of 3 mm in diameter and 3 mm in thickness was established in both knees of 18 New Zealand white rabbits (aged 28-35 weeks; weighing, 2.1-2.8 kg), and divided into 3 groups randomly, 6 rabbits in each group: LIPUS group, common group, and model group. Defect was repaired with LIPUS-intervention gel composite, non LIPUS-intervention gel composite in LIPUS group and common group, respectively; defect was not treated in the model group. The general condition of rabbits was observed after operation. The repair effect was evaluated by gross and histological observations, immunohistochemical staining, and Wakitani score at 8 and 12 weeks after operation. Results Defect was filled with hyaline chondroid tissue and white chondroid tissue in LIPUS and common groups, respectively. LIPUS group was better than common group in the surface smooth degree and the degree of integration with surrounding tissue. Defect was repaired slowly, and the new tissue had poor elasticity in model group. Histological observation and Wakitani score showed that LIPUS group had better repair than common group at 8 and 12 weeks after operation; the repair effect of the 2 groups was significantly better than that of model group (P lt; 0.05); and significant differences in repair effect were found between at 8 and 12 weeks in LIPUS and common groups (P lt; 0.05). The collagen type II positive expression area and absorbance (A) value of LIPUS and common groups were significantly higher than those of model group (P lt; 0.05) at 8 and 12 weeks after operation, and the expression of LIPUS group was superior to that of common group at 12 weeks (P lt; 0.05); and significant differences were found between at 8 and 12 weeks in LIPUS group (P lt; 0.05), but no significant difference between 2 time points in common and model groups (P gt; 0.05). Conclusion Allogeneic chondrocytes-calcium alginate gel composite can effectively repair articular cartilage defect. The effect of LIPUS optimized allogeneic chondrocytes-calcium alginate gel composite is better.