Objective To study the effect of autogenous bone marrow on guided bone regeneration (GBR),and evaluate the repairing ability of GBR in bone defect with autogenous bone marrow. Methods Ten mm segmental defects were produced in both radii of 18 rabbits. The defect was bridged with a silicon tube. Autogenous bone marrow was injected into the tube on the experimental group at 0, 2,4 weeks after operation, and peripheralblood into the control group at thesame time. The X-ray, gross, histological and biochemical examinations were observed invarious times. Results The new bone formation of experimental group was prior to that of control group; calcium and alkaline phosphatase of experimental groupwere higher than those of control group. The experimental group had all been healed at the tenth week, but no one healed in control group. Conclusion It can be conclude that autogenous bone marrow can stimulate bone formation and facilitate GBR in bone defect.
OBJECTIVE To confirm membrane-guided tissue regeneration in the healing course of segmental bone defects and study the mechanism. METHODS Segmental, 1 cm osteoperiosteal defects were produced in both radii of 12 rabbits. One side was covered with hydroxyapatite/polylactic acid(HA/PLA) membrane encapsulated as a tube. The contralateral side served as an untreated control. Healing courses were detected by radiographic and histologic examinations. RESULTS All control sides showed nonunion, whereas there were consistent healing pattern in test sides. CONCLUSION Membrane technique can promote bone regeneration.
With the in-depth research on bone repair process, and the progress in bone repair materials preparation and characterization, a variety of artificial bone substitutes have been fully developed in the treatment of bone related diseases such as bone defects. However, the current various natural or synthetic biomaterials are still unable to achieve the structure and properties of natural bone. Carbon nanotubes (CNTs) have provided a new direction for the development of new materials in the field of bone repair due to their excellent structural stability, mechanical properties, and functional group modifiability. Moreover, CNTs and their composites have broad prospects in the design of bone repair materials and as drug delivery carriers. This paper describes the advantages of CNTs related to bone tissue regeneration from the aspects of morphology, chemistry, mechanics, electromagnetism, and biosafety, as well as the application of CNTs in drug delivery carriers and reinforcement components of scaffold materials. In addition, the potential problems and prospects of CNTs in bone regenerative medicine are discussed.
ObjectiveTo prepare a bone tissue engineering scaffold for repairing the skull defect of Sprague Dawley (SD) rats by combining exogenous transforming growth factor β1 (TGF-β1) with gelatin methacryloyl (GelMA) hydrogel.MethodsFirstly, GelMA hydrogel composite scaffolds containing exogenous TGF-β1 at concentrations of 0, 150, 300, 600, 900, and 1 200 ng/mL (set to groups A, B, C, D, E, and F, respectively) were prepared. Cell counting kit 8 (CCK-8) method was used to detect the effect of composite scaffold on the proliferation of bone marrow mesenchymal stem cells (BMSCs) in SD rats. ALP staining, alizarin red staining, osteocalcin (OCN) immunofluorescence staining, and Western blot were used to explore the effect of scaffolds on osteogenic differentiation of BMSCs, and the optimal concentration of TGF-β1/GelMA scaffold was selected. Thirty-six 8-week-old SD rats were taken to prepare a 5 mm diameter skull bone defect model and randomly divided into 3 groups, namely the control group, the GelMA group, and the GelMA+TGF-β1 group (using the optimal concentration of TGF-β1/GelMA scaffold). The rats were sacrificed at 4 and 8 weeks after operation, and micro-CT, HE staining, and OCN immunohistochemistry staining were performed to observe the repair effect of skull defects.ResultsThe CCK-8 method showed that the TGF-β1/GelMA scaffolds in each group had a promoting effect on the proliferation of BMSCs. Group D had the strongest effect, and the cell activity was significantly higher than that of the other groups (P<0.05). The results of ALP staining, alizarin red staining, OCN immunofluorescence staining, and Western blot showed that the percentage of ALP positive area, the percentage of alizarin red positive area, and the relative expressions of ALP and OCN proteins in group D were significantly higher than those of the other groups (P<0.05), the osteogenesis effect in group D was the strongest. Therefore, in vitro experiments screened out the optimal concentration of TGF-β1/GelMA scaffold to be 600 ng/mL. Micro-CT, HE staining, and OCN immunohistochemistry staining of rat skull defect repair experiments showed that the new bone tissue and bone volume/tissue volume ratio in the TGF-β1+GelMA group were significantly higher than those in the GelMA group and control group at 4 and 8 weeks after operation (P<0.05).ConclusionThe TGF-β1/GelMA scaffold with a concentration of 600 ng/mL can significantly promote the osteogenic differentiation of BMSCs, can significantly promote bone regeneration at the skull defect, and can be used as a bioactive material for bone tissue regeneration.
Bone morphogenetic protein (BMPs) has been so far regarded as one of the highly potent osteoinductive growth factors. Recombinant human bone morphogenetic proteins have been utilized extensively in the disciplines of orthopedics, stomatology, etc. For clinical application, BMPs are usually loaded in carriers with a controlled-release system, to maintain concentration to induce de novo bone formation at the desired site. In this article, the research advancements of the carriers and release systems of BMP are reviewed.
Parathyroid hormone (PTH) exerts multiple effects such as regulating bone remodeling, promoting angiogenesis, etc., and it is an active factor with great application potential for bone repair. In recent years, with the development of scaffold material loading strategies and parathyroid hormone-related peptides (PTHrPs), in situ loading of PTH or PTHrPs on scaffold materials to promote bone defect healing gradually becomes possible. Based on the current status and challenges of intermittent PTH (iPTH) for bone tissue engineering, the review summarizes the in-situ application strategies of PTH and the construction of PTHrPs as well as current problems and further directions in this field, with a view to propel the clinical application of scaffold materials loaded with PTH or PTHrPs in situ.
ObjectiveTo observe the change of stromal cell-derived factor 1α/cysteine X cysteine receptor 4 (SDF-1α/CXCR4) signaling pathway during the process of axial stress stimulation promoting bone regeneration, and to further explore its mechanism.MethodsA total of 72 male New Zealand white rabbits were selected to prepare the single cortical bone defect in diameter of 8 mm at the proximal end of the right tibia that repaired with deproteinized cancellous bone. All models were randomly divided into 3 groups (n=24). Group A was treated with intraperitoneally injection of PBS; Group B was treated with stress stimulation and intraperitoneally injection of PBS; Group C was treated with stress stimulation and intraperitoneally injection of AMD3100 solution. The X-ray films were taken and Lane-Sandhu scores of bone healing were scored at 2, 4, 8, and 12 weeks after operation, while specimens were harvested for HE staining, immunohistochemical staining of vascular endothelial growth factor (VEGF) and CXCR4, and Western blot (SDF-1α and CXCR4). The bone healing area was scanned by Micro-CT at 12 weeks after operation, and the volume and density of new bone were calculated.ResultsX-ray film showed that the Lane-Sandhu scores of bone healing in group B were significantly higher than those in groups A and C at 4, 8, and 12 weeks after operation (P<0.05). Micro-CT scan showed that the bone defect was repaired in group B and the pulp cavity was re-passed at 12 weeks after operation. The volume and density of new bone were higher in group B than in groups A and C (P<0.05). HE staining showed that the new bone growth in bone defect area and the degradation of scaffolds were faster in group B than in groups A and C after 4 weeks. The immunohistochemical staining showed that the expressions of VEGF and CXCR4 in 3 groups reached the peak at 4 weeks, and group B was higher than groups A and C (P<0.05). Western blot analysis showed that the expressions of SDF-1α and CXCR4 in group B were significantly higher than those in groups A and C at 4 and 8 weeks after operation (P<0.05).ConclusionAxial stress stimulation can promote the expression of SDF-1α in bone defect tissue, activate and regulate the CXCR4 signal collected by marrow mesenchymal stem cells, and accelerate bone regeneration in bone defect area.
ObjectiveBased on the cell-extracellular matrix adhesion theory in selective cell retention (SCR) technology, demineralized bone matrix (DBM) modified by simplified polypeptide surface was designed to promote both bone regeneration and angiogenesis.MethodsFunctional peptide of α4 chains of laminin protein (LNα4), cyclic RGDfK (cRGD), and collagen-binding domain (CBD) peptides were selected. CBD-LNα4-cRGD peptide was synthesized in solid phase and modified on DBM to construct DBM/CBD-LNα4-cRGD scaffold (DBM/LN). Firstly, scanning electron microscope and laser scanning confocal microscope were used to examine the characteristics and stability of the modified scaffold. Then, the adhesion, proliferation, and tube formation properties of CBD-LNα4-cRGD peptide on endothelial progenitor cells (EPCs) were detected, respectively. Western blot method was used to verify the molecular mechanism affecting EPCs. Finally, 24 10-week-old male C57 mice were used to establish a 2-mm-length defect of femoral bone model. DBM/LN and DBM scaffolds after SCR treatment were used to repair bone defects in DBM/LN group (n=12) and DBM group (n=12), respectively. At 8 weeks after operation, the angiogenesis and bone regeneration ability of DBM/LN scaffolds were evaluated by X-ray film, Micro-CT, angiography, histology, and immunofluorescence staining [CD31, endomucin (Emcn), Ki67].ResultsMaterial related tests showed that the surface of DBM/LN scaffold was rougher than DBM scaffold, but the pore diameter did not change significantly (t=0.218, P=0.835). After SCR treatment, DBM/LN scaffold was still stable and effective. Compared with DBM scaffold, DBM/LN scaffold could adhere to more EPCs after the surface modification of CBD-LNα4-cRGD (P<0.05), and the proliferation rate and tube formation ability increased. Western blot analysis showed that the relative expressions of VEGF, phosphorylated FAK (p-FAK), and phosphorylated ERK1/2 (p-ERK1/2) proteins were higher in DBM/LN than in DBM (P<0.05). In the femoral bone defect model of mice, it was found that mice implanted with DBM/LN scaffold had stronger angiogenesis and bone regeneration capacity (P<0.05), and the number of CD31hiEmcnhi cells increased significantly (P<0.05).ConclusionDBM/LN scaffold can promote the adhesion of EPCs. Importantly, it can significantly promote the generation of H-type vessels and realize the effective coupling between angiogenesis and bone regeneration in bone defect repair.
Objective To evaluate the effect of internal fixation on the stability of pedicled fascial flap and the osteogenesis of exceed critical size defect (ECSD) of bone so as to provide theory for the clinical application by the radiography and histology observation. Methods The ECSD model of the right ulnar midshaft bone and periosteum defect of 1 cm in length was established in 32 New Zealand white rabbits (aged 4-5 months), which were divided into group A and group B randomly (16 rabbits in each group). The composite tissue engineered bone was prepared by seeding autologous red bone marrow (ARBM) on osteoinductive absorbing material (OAM) containing bone morphogenetic protein and was used repair bone defect. A pedicled fascial flap being close to the bone defect area was prepared to wrap the bone defect in group A (control group). Titanium miniplate internal fixation was used after defect was repair with composite tissue engineered bone and pedicled fascial flap in group B (experimental group). At 2, 4, 6, and 8 weeks, the X-ray films examination, morphology observation, and histology examination were performed; and the imaging 4-score scoring method and the bone morphometry analysis was carried out. Results All rabbits survived at the end of experiment. By X-ray film observation, group B was superior to group A in the bone texture, the space between the bone ends, the radiographic changes of material absorption and degradation, osteogenesis, diaphysis structure formation, medullary cavity recanalization. The radiographic scores of group B were significantly higher than those of group A at different time points after operation (P lt; 0.05). By morphology and histology observation, group B was superior to group A in fascial flap stability, tissue engineered bone absorption and substitution rate, external callus formation, the quantity and distribution area of new cartilage cells and mature bone cells, and bone formation such as bone trabecula construction, mature lamellar bone formation, and marrow cavity recanalization. The quantitative ratio of bone morphometry analysis in the repair area of group B were significantly larger than those of group A at different time points after operation (P lt; 0.05). Conclusion The stability of the membrane structure and the bone defect area can be improved after the internal fixation, which can accelerate bone regeneration rate of the tissue engineered bone, shorten period of bone defect repair, and improve the bone quality.
Objective To summarize the research progress of controlled release of angiogenic factors and osteogenic factors in bone tissue engineering. Methods The domestic and abroad literature on the controlled release structure of growth factors during bone regeneration in recent years was extensively reviewed and summarized. Results The sustained-release structure includes direct binding, microsphere-three-dimensional scaffold structure, core-shell structure, layer self-assembly, hydrogel, and gene carrier. A sustained-release system composed of different sustained-release structures combined with different growth factors can promote bone regeneration and angiogenesis. Conclusion Due to its controllability and persistence, the growth factor sustained-release system has become a research hotspot in bone tissue engineering and has broad application prospects.